Abstract:Due to the low price and good comprehensive properties, FRP composite material has become a new type of civil application material in recent years. In this paper, Araldite® 2012 adhesive was used to bond basalt-fiber-reinforced polymer (BFRP), and the durability of its bonded joints was investigated. Experiments were carried out at 80 °C/DI water (deionized water), 80 °C/3.5% NaCl solution (3.5% SS), and 80 °C/5.0% NaCl solution (5.0% SS) at 0- (unaged), 10-, 20-, and 30-day aging. The specimen and BFRP in the environment of 80 °C/DI water, 80 °C/3.5% SS, and 80 °C/5.0% SS found salt solution under the condition of all sample water absorption decreases, and the activity of salt solution chemistry was weaker compared with deionized water. The load-displacement curve of the joint failure was obtained through quasi-static tensile experiments, and it was found that the adhesive would undergo a post-curing reaction that had a positive impact on the stiffness of the joint in a high-temperature environment. At the same time, it was found that the joint failure strength decreased less in the salt solution environment, and deionized water was more destructive than the salt solution. Referring to the change in water absorption, it was found that the change in the mechanical properties of the joint was mainly related to the permeation effect of the polymer. The change in the Tg of adhesive was measured by differential scanning calorimetry (DSC). It was found that Tg would decrease after aging, and the change in Tg was mainly related to the mobility of the molecular chain. Thermogravimetric analysis (TGA) was used to analyze the thermal behavior of the epoxy resin and some organic matter, and the main weight loss stage was 340-450 °C, which was the complete degradation of epoxy resin and some organic matter. Macro visual and microscopic scanning electron microscope (SEM) and energy dispersive X-ray spectroscopy (EDX) were used to analyze the failure section, and it can be concluded that the failure mode of joint tear failure transitioned to cohesion in the late-mixed interface failure, at the visible interface between the fiber and the resin matrix.

Durability of Structural Adhesive Exposed to Marine Environment

Effect of chloride penetration on CFRP sheet, CFRP‐concrete interface, and CFRP‐strengthened concrete beams

A Systematic Study on the Failure Behaviors of Aluminum Alloy/composite Bonded Joints Exposed to Various Typical Aging Environments for Automobiles

Durability of components of FRP-concrete bonded reinforcement systems exposed to chloride environments

Durability related environmental zonation and design methodology for marine RC structures

Durability of Frp Concrete Bonds and Its Constituent Properties under the Influence of Moisture Conditions

Long-Term Performance of External Bonding under Moisture and Temperature Effects

Durability Performances of Carbon Fiber-Reinforced Polymer and Concrete-Bonded Systems under Moisture Conditions

Accelerating Tests For The Performance Deterioration Of Concrete Exposed To Chloride Media

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Influence of Stochastic Chlorine Environment on the Spatiotemporal Deterioration of Marine RC Structures

Chloride penetration in concrete under marine atmospheric environment – analysis of the influencing factors

Study on the Effect of Salt Solution on Durability of Basalt-Fiber-Reinforced Polymer Joints in High-Temperature Environment

Influence of Initial Curing Conditions and Exposure Environments on Chloride Migration in Concrete Using Electrochemical Method

Interfacial Study of Steel Joints Prepared with a Catechol-Modified Epoxy Adhesive with Enhanced Bonding Performance and Durability

Fracture durability of composite–titanium adhesively bonded structures exposed to seawater environment

Experimental study on AFRP-to-concrete bond behavior subjected to underground water

Durability of anticorrosive-coated steel–carbon fiber reinforced polymer structural adhesive joint at high temperature and humidity

Effects of Moisture Ingress on the Mesoscale Mechanical Properties of Epoxy Adhesives under Elevated Temperature

Unraveling disadhesion mechanism of epoxy/CSH interface under aggressive conditions

Predicting Degradation of Composite-Titanium Adhesively Bonded Joints Exposed to Seawater Environment