Abstract:Purpose This study aims to investigate the thermal fracture mechanism of moisture-preconditioned SAC305 ball grid array (BGA) solder joints subjected to multiple reflow and thermal cycling. Design/methodology/approach The BGA package samples are subjected to JEDEC Level 1 accelerated moisture treatment (85 °C/85%RH/168 h) with five times reflow at 270 °C. This is followed by multiple thermal cycling from 0 °C to 100 °C for 40 min per cycle, per IPC-7351B standards. For fracture investigation, the cross-sections of the samples are examined and analysed using the dye-and-pry technique and backscattered scanning electron microscopy. The packages' microstructures are characterized using an energy-dispersive X-ray spectroscopy approach. Also, the package assembly is investigated using the Darveaux numerical simulation method. Findings The study found that critical strain density is exhibited at the component pad/solder interface of the solder joint located at the most distant point from the axes of symmetry of the package assembly. The fracture mechanism is a crack fracture formed at the solder's exterior edges and grows across the joint's transverse section. It was established that Au content in the formed intermetallic compound greatly impacts fracture growth in the solder joint interface, with a composition above 5 Wt.% Au regarded as an unsafe level for reliability. The elongation of the crack is aided by the brittle nature of the Au-Sn interface through which the crack propagates. It is inferred that refining the solder matrix elemental compound can strengthen and improve the reliability of solder joints. Practical implications Inspection lead time and additional manufacturing expenses spent on investigating reliability issues in BGA solder joints can be reduced using the study's findings on understanding the solder joint fracture mechanism. Originality/value Limited studies exist on the thermal fracture mechanism of moisture-preconditioned BGA solder joints exposed to both multiple reflow and thermal cycling. This study applied both numerical and experimental techniques to examine the reliability issue.

Reflow Profile Optimization of Μbga Solder Joints Considering Reflow Temperature and Time Coupling

Predicting fatigue life of Solder joint with submodel method for a BGA package

Smarter Temperature Setup for Reflow Oven to Minimize Temperature Variation Among Components

New Reliability Assessment Method for Solder Joints in BGA Package by Considering the Interaction between Design Factors

Optimization Method for Hot Air Reflow Soldering Process Based on Robust Design

Determination of Smarter Reflow Profile to Achieve a Uniform Temperature Throughout a Board

Thermal profiling: a reflow process based on the heating factor

Simulation analysis of residual stress of BGA solder joints after reflow soldering based on element birth and death technology

Reliability Optimisation and Lifetime Modelling of micro-BGA Assemblies in Harsh Environment Applications

Reliability Evaluation Method for Electronic Device BGA Package Considering the Interaction Between Design Factors

Thermal fatigue life prediction and intermetallic compound behaviour of SAC305 BGA solder joints subject to accelerated thermal cycling test

Analysis of residual stress after reflow soldering of QFN package

Reliability Evaluation of Board-Level Flip-Chip Package under Coupled Mechanical Compression and Thermal Cycling Test Conditions

Finite element method and experimental study on life prediction of lead-free BGA solder joints using an energy-based approach

Optimization of the Boundary Conditions of a Board Level Reliability Test Board to Maximize the Fatigue Life of Ball Grid Array Solder Joints under Thermal Cycling and Random Vibration

On reflow soldering process and reflow profile

Comparative study of machine learning method and response surface methodology in BGA solder joint parameter optimization

Survey on Fatigue Life Prediction of BGA Solder Joints

Investigation of Long-Term Reliability and Failure Mechanism of Solder Interconnections with Multifunctional Micro-Moiré Interferometry System