Enhanced piezoelectric properties of (1 - x)BiFe 0.98 (Zn 0.5 Hf 0.5 ) 0.02 O 3 -xBaTiO 3 ceramics near the morphotropic phase boundary.
Yunjing Shi,Hairui Bai,Fei Yan,Rui Hu,Kaikai Chen,Bo Shen,Jiwei Zhai
DOI: https://doi.org/10.1039/c9dt04664j
IF: 4
2020-01-01
Dalton Transactions
Abstract:Here, (1 - x)BiFe0.98(Zn0.5Hf0.5)(0.02)O-3-xBaTiO(3) + 1 mol% MnO2 (x = 0.225, 0.250, 0.265, 0.275, 0.285, and 0.300) (BFZH-xBT) ceramics were synthesized using a traditional ceramic sintering technique. A morphotropic phase boundary (MPB) consisting of rhombohedral (R) and tetragonal (T) phases was formed in the BFZH-xBT ceramics when x = 0.285. The suitable content of BT was conducive to enlarge the particle size, improve ferroelectric and piezoelectric properties, and reduce the leakage current density. For the optimal component at x = 0.285, we observed the largest grain size, a lowest leakage current density value of similar to 1.93 x 10(-5) A cm(-2), minimum content of oxygen vacancies, high temperature of 478 degrees C and the highest piezoelectric coefficient (d(33)) of 130 pC N-1.