Abstract:Samples of square-edged timbers of fir and ribbed birch with defects of holes, flaws or knots were tested by thermal infrared imager and infrared lamp. Each sample had only one defect of the three kinds of them. There're 5 fir samples, two samples with a hole in the middle, one with a hole in either side, and the other two samples with flaws and knots, respectively. Three are 3 samples of ribbed birch, one sample with a hole in the middle of it, the other two samples with flaws and knots, respectively. It could be found out by comparing experiments results that infrared thermal imager could detect holes in the middle, flaws and knots of fir and ribbed birch samples correctly and distinctly, but couldn't distinguish the kind of defects. It couldn't detect the holes at the sides of fir samples. Areas of holes and knots had lower temperature and areas of knots had higher temperature. Different testing conditions were necessary in order to detect different defects correctly. Holes in the middle of samples of both fir and ribbed birch could be detected only by double-way detecting model, while flaws could be detected only by one-way detecting model. Knots of fir samples could be detected only by one-way detecting model. Knots of ribbed birch samples could be detected by both one-way and double-way detecting models. The size and position of defects could be determined more accurately with higher moisture content, though the heating time by infrared lamp would be longer.

Nondestructive Testing of Wood Defects by ESSPI

Application of Electronic Shearography Speckle Pattern Interferomety to Nondestructive Testing of Wood Material

Detection of Knot Defects on Coniferous Wood Surface Using Near Infrared Spectroscopy and Chemometrics

Non-destructive Test of Multiply Plywood Using ESSPI with Wide Audio-Frequency Driving Vibration

Non-destructive Testing of Wood Defects Based on Discriminant Analysis Method

Non-Destructive Testing of Wood Defects Based on Ultrasonic Technology

Nondestructive Testing of Wood Defects Based on Stress Wave Technology

Non-destructive Testing of Wood Defects for Korean Pine in Northeast China Based on Ultrasonic Technology

Nondestructive Testing of Wood Hole Defect by Ultrasonic Spectrum Analysis

Current Situaton of Research on the Non—Destructive Testing Technique for Wood Defects

The Depth Measurement of Internal Defect Based on Laser Speckle Shearing Interference

An air-coupled ultrasonic imaging system for non-destructive wood testing

Nondestructive Testing of Thin Composite Structures for Subsurface Defects Detection Using Dynamic Laser Speckles

Potential of Near-infrared Spectroscopy to Detect Defects on the Surface of Solid Wood Boards

Digital shearing speckle for nondestructive testing of composite materials

Research on Stress Wave Tomography of Spruce Logs with Artificial Defects under Different Number Sensors

Propagation Velocity Model and Two-Dimensional Defect Imaging of Stress Wave in Larch (larix Gmelinii) Wood

Effect of Sensor Quantity on Measurement Accuracy of Log Inner Defects by Using Stress Wave

Research on detecting defects of square-edged timber of fir and ribbed birch by infrared thermal imager: A study on nondestructive testing of wood defects by infrared thermal imager

Grain effect on the accuracy of defect detection in wood structure by using acoustic-laser technique

Nondestructive testing by ESPI and quasi phase shift gradient technique