Abstract:Two ethylene/1-butene/1-hexene terpolymers (sample A and sample B) produced in the fluidized bed polymerization reactor with two different operation modes were fractionated by prepared temperature rising elution fractionation (P-TREF), and the structures of obtained fractions were characterized by the gel permeation chromatography (GPC), differential scanning calorimetry (DSC), nuclear magnetic resonance (13C-NMR), and successive self-nucleation and annealing thermal analysis (SSA). Meanwhile, the tensile yield strength, tensile strength, impact strength, elongation and haze of these two sampled were also tested according to the National Standard of the People 's Republic of China. Results showed that compared with sample B produced in the condensed operation mode, the sample A produced in the liquid containing operation mode had better tensile yield strength, tensile strength, impact strength, elongation and haze. The relative content and the molecular weight of the low-temperature elution fraction of sample A was lower than those of sample B, but for high-temperature elution fraction, the relative content and the molecular weight of sample A were both higher than those of sample B. Sample A possessed the broader distribution of lamellar thickness than sample B. The distribution of short branches between molecular chains of sample A was also wider than that of sample B. From the analysis of branching degree and molecular weight, sample A's short chain branches were more likely to grow in the high molecular weight chains than sample B. In summary, the sample A produced in the liquid containing operation mode has more excellent physical performance than sample B produced in the condensed operation mode, which was suitable for the preparation of high-performance stretch film material.

Synthesis and Characterization of Short-Chain Branched Polyethylene

The Copolymerization of Ethylene and Polar Comonomers for the Preparation of Functional Hyperbranched Polyethylene

Synthesis Of Ethylene/Vinyl Ester Copolymers With Pendent Linear Branches Via Ring-Opening Metathesis Polymerization Of Fatty Acid-Derived Cyclooctenes

Chain Structure and Mechanical Properties of Ethylene Copolymers in Two Operating Modes of Fluidized Bed Polymerization Reactor

Dynamic Mechanical and Rheological Properties of Metallocene-Catalyzed Long-Chain-Branched Ethylene/Propylene Copolymers

Molecular Dynamics Study of the Conformation and Dynamics of Precisely Branched Polyethylene

Effect of Short Chain Branching Distribution on Crystallization of Ethylene-Butene Copolymers

Nonisothermal Crystallization Kinetics of Ethylene-Butene Copolymer/Low-Density Polyethylene Blends

Synthesis and Characterization of Branched Polyethylene by Ethylene Homopolymerization with Monotitanocene and Modified Methylaluminoxane Catalysts

Synthesis Of Long-Chain-Branched Polyethylene By Ethylene Homopolymerization With A Novel Nickel(Ii) Alpha-Diimine Catalyst

SYNTHESIS AND PROPERTIES OF LONG CHAIN BRANCHED POLYETHYLENE WITH BINARY CATALYST SYSTEM

Branched Polyethylene Prepared Byin Situ Copolymerization of Ethylene with Monotitanocene and Modified Methylaluminoxane Catalyst

Synthesis of Long-Chain Branch Polyethylene by Ethylene Homopolymerization over Novel Mono-Titanocene Catalysts

Synthesis and characterization of atactic poly(1-butene) and polyethylene-poly(1-butene) block copolymer

The Effect Of Comonomer Type And Content On The Properties Of Ziegler-Natta Bimodal High-Density Polyethylene

Controllable Preparation of Branched Polyolefins with Various Microstructural Units Via Chain-walking Ethylene and Pentene Polymerizations

Structure and properties of branched polyethylene

Lowly branched-highly branched block polyethylene: Synthesis, characterization and application

Synthesis of Propylene/1-Butene Copolymers Catalyzed by Ziegler-Natta Catalyst and Their Characterization

Synthesis and thermal analysis of in-chain multi-functionalized Polybutadiene using 1,1-Bis(4-dimethylaminophenyl)ethylene

Syntheses of Branched Polyolef Ins