Chain Structure and Mechanical Properties of Ethylene Copolymers in Two Operating Modes of Fluidized Bed Polymerization Reactor
Xiao-bo Hu,Yao Yang,Bin-bo Jiang,Jing-dai Wang,Yong-rong Yang
DOI: https://doi.org/10.11777/j.issn1000-3304.2020.20140
2021-01-01
Acta Polymerica Sinica
Abstract:Two ethylene/1-butene/1-hexene terpolymers (sample A and sample B) produced in the fluidized bed polymerization reactor with two different operation modes were fractionated by prepared temperature rising elution fractionation (P-TREF), and the structures of obtained fractions were characterized by the gel permeation chromatography (GPC), differential scanning calorimetry (DSC), nuclear magnetic resonance (13C-NMR), and successive self-nucleation and annealing thermal analysis (SSA). Meanwhile, the tensile yield strength, tensile strength, impact strength, elongation and haze of these two sampled were also tested according to the National Standard of the People 's Republic of China. Results showed that compared with sample B produced in the condensed operation mode, the sample A produced in the liquid containing operation mode had better tensile yield strength, tensile strength, impact strength, elongation and haze. The relative content and the molecular weight of the low-temperature elution fraction of sample A was lower than those of sample B, but for high-temperature elution fraction, the relative content and the molecular weight of sample A were both higher than those of sample B. Sample A possessed the broader distribution of lamellar thickness than sample B. The distribution of short branches between molecular chains of sample A was also wider than that of sample B. From the analysis of branching degree and molecular weight, sample A's short chain branches were more likely to grow in the high molecular weight chains than sample B. In summary, the sample A produced in the liquid containing operation mode has more excellent physical performance than sample B produced in the condensed operation mode, which was suitable for the preparation of high-performance stretch film material.