Abstract:<p>Polypropylene (PP) has been commonly used as packaging materials due to the favorable mechanical and optical properties related to its diverse and complex chain microstructure which can be better understood through effective fractionation. In this work, two commercial PP resins (A and B) with similar bimodal melting temperature distribution in the range of 100–160 °C but different ethylene content (9.1–12.3 mol%) are fractionated by preparative temperature rising elution fractionation (P-TREF) and relevant fractions are characterized by a variety of techniques such as high temperature-gel permeation chromatography (HT-GPC), differential scanning calorimetry (DSC), <sup>13</sup>C nuclear magnetic resonance (NMR) spectroscopy, Fourier transform-infrared (FT-IR) spectroscopy, and wide-angle X-ray diffraction (WAXD). The chain microstructures of the two resins used as food packaging film exhibit heterogeneity and some differences, which are mainly caused by broad and different distribution of ethylene comonomers. Resin B contains more ethylene units than resin A, and the ethylene units are incorporated into the PP chains in the forms of individual unit or very short segments, resulting in large amount of fractions with relatively low isotacticity and crystallinity that eluted at the temperature range of 35–90 °C. These fractions account for 84.07 wt% of resin B, whereas 59.66 wt% of resin A. The propylene sequences of different isotacticity and crystallinity generated by the insertion of ethylene comonomers in resin B are mainly responsible for its biomodal melting behavior. However, ethylene comonomers tend to insert into the PP chains of resin A in the forms of long polyethylene (PE) blocks and generate propylene−ethylene block copolymers with high crystallizability which can be eluted at high temperatures of 120–140 °C. These fractions constitute 3.16 wt% of resin A, but barely exist in resin B. Moreover, 35.83 wt% of resin A were eluted at 110 °C, whereas only 13.22 wt% of resin B can be eluted at this temperature. These fractions with high isotacticity and molecular weight eluted at high temperatures contribute to the higher flexural modulus of resin A. Both long ethylene blocks and propylene sequences of different lengths contribute to the biomodal melting peaks on the thermogram of resin A.</p>

Chain Structure and Mechanical Properties of Ethylene Copolymers in Two Operating Modes of Fluidized Bed Polymerization Reactor

Influence of Chain Microstructure on Ethylene-Norbornene Copolymer Film Properties

Investigation of a Dynamic Operation Mode of Ethylene Polymerization Process with a Liquid-Containing Fluidized Bed

Dynamic Mechanical and Rheological Properties of Metallocene-Catalyzed Long-Chain-Branched Ethylene/Propylene Copolymers

Liquid Containing Particle Polymerization: Ethylene/-Olefin Reaction in a New Environment

Thermal and Mechanical Properties of Ultrahigh-Molecular-Weight Ethylene/1-Hexene Copolymers Prepared by Living Polymerization with Fluorinated Bis(Phenoxy-Imine) Titanium(Iv) Catalyst

Structure Analysis of Ethylene/1-Octene Copolymers Synthesized from Living Coordination Polymerization

Synthesis, characterization and lubricating effect of long chain branched polydimethylsiloxane-g-polyethylene copolymers

Studies on composition and molecular structure of high impact polypropylene

Comparison of chain microstructure between two propylene−ethylene copolymer resins with bimodal melting temperature distribution

Dynamic Rheology Behavior of Bimodal Polyethylene

Tensile Behaviour of Homogeneous Ethylene Copolymers

Synthesis and Characterization of Short-Chain Branched Polyethylene

The Structure Characterization of Ethylene-Propylene Random Copolymers for Hot Water Piping

The Chain Microstructure And Condensed Structure Of Polyethylene Resin Used For Biaxially Stretched Film

Comparison of chain structures between high-speed extrusion coating polyethylene resins by preparative temperature rising elution fractionation and cross-fractionation

Chain microstructure of two in-reactor alloy impact polypropylene resins with same stiffness and different toughness

Elucidation of the relationships of structure-process-property for different ethylene/α-olefin copolymers during film blowing: An in-situ synchrotron radiation X-ray scattering study

Chain microstructure comparison of two transparent polypropylene resins fractionated by temperature rising elution fractionation

The Effect Of Comonomer Type And Content On The Properties Of Ziegler-Natta Bimodal High-Density Polyethylene

Structure-rheology properties of polyethylenes with varying macromolecular architectures