Abstract:Based on the characteristics that Cat.Ni /MAO can keep "living manner" in a certain reaction time and its "chain walking" behavior is significantly affected by reaction temperature, polyethylenes with lowly branched-highly branched block structure were synthesized by switching the reaction temperature with ethylene as the sole monomer. The lowly branched-highly branched structure of the obtained block polyethylene was proved by the evidences coming form 13 C NMR, DSC and GPC. The tensile test results show that the polyethylenes with lowly branched-highly branched block structure perform well in tensile properties. The tensile properties are related to the block composition. The "soft" segment is beneficial to the increase of elongation at break, while the "hard" segment contributes more to the increase of modulus. The obtained block polyethylenes perform very well as a compatibilizer for HDPE/LDPE blends. The change trends of the tensile curves of the blends after adding the compatibilizer are almost consistent with that of HDPE.

Lowly branched-highly branched block polyethylene: Synthesis, characterization and application