Deposition of REBCO with different rare earth elements on CeO2 buffered technical substrates by fluorine-free metal organic decomposition route
Jiangtao Shi,Yue Zhao,Guangyu Jiang,Jiamin Zhu,Yue Wu,Yusong Gao,Xueling Quan,Xin Yu,Wei Wu,Zhijian Jin
DOI: https://doi.org/10.1016/j.jeurceramsoc.2021.04.001
IF: 5.7
2021-08-01
Journal of the European Ceramic Society
Abstract:<p>Pristine <em>RE</em>Ba<sub>2</sub>Cu<sub>3</sub>O<sub>7−</sub><em><sub>δ</sub></em> (<em>RE</em>BCO, <em>RE</em> with Yb, Y, Dy, Gd, Eu and Sm) superconducting films are deposited on CeO<sub>2</sub> buffered technical substrates by fluorine-free metal organic decomposition (FF-MOD) method. The structure and superconductivity are comprehensively characterized and studied. Under the optimal conditions, all the films form good crystallinity and strong biaxial texture examined by XRD. A smooth and dense morphology is observed in the YBCO, GdBCO, EuBCO and SmBCO films. For all the films, <em>T</em><sub>c</sub><sup>onset</sup> values are lower than that in the corresponding bulk materials, implying a certain degree of microstructure defects (e.g., <em>RE</em>-Ba substitution, and/or oxygen vacancies). Among all the compositions, the GdBCO film shows a high <em>T</em><sub>c</sub><sup>onset</sup> value (>90 K), while the high <em>J</em><sub>c</sub> values are achieved at 77 K in broad field regime, also being with the largest maximum pinning force of 2.3 GN m<sup>-3</sup>. On the other hand, a high <em>J</em><sub>c</sub> value (at 77 K self-field) is obtained in the YBCO film, however, the rapid <em>J</em><sub>c</sub> decay with increase of the magnetic fields is found. These results reveal that defects in the YBCO film could only serve as weak pinning centers at least at 77 K. According to Dew-Hughes fitting models, we found that the primary pinning mechanism in all the <em>RE</em>BCO films attributes to typical 2D non-superconducting phase i.e., Normal surface pinning. This work for the first time systemically demonstrates feasibility of deposition <em>RE</em>BCO with various rare earth elements on technical substrates through the FF-MOD route, and provides a guideline for further growth of nano-composited and mixed rare earth <em>RE</em>BCO films.</p>
materials science, ceramics