Abstract:In order to provide the necessary phase equilibria data for understanding the development of the Widmanstatten pattern in iron meteorites, we have redetermined the Fe-Ni-P phase diagram from 0 to 100 pct Ni, 0 to 16.5 wt pct P, in the temperature range 1100° to 550°C. Long term heat treatments and 130 selected alloys were used. The electron microprobe was employed to measure the composition of the coexisting phases directly. We found that the fourphase reaction isotherm, where α+ liq ⇌ γ+ Ph, occurs at 1000° ± 5°C. Above this temperature the ternary fields α+ Ph + liq and α+ γ+ liq are stable and below 1000°C, the ternary fields ⇌+ γ + Ph and γ + Ph + liq are stable. Below 875°C a eutectic reaction, liq → γ + Ph, occurs at the Ni-P edge of the diagram. Altogether nineteen isotherms were determined in this study. The phase boundary compositions of the two-and three-phase fields are listed and are compared with the three binary diagrams. The α + γ + Ph field expands in area in each isotherm as the temperature decreases from 1000°C. Below 800°C the nickel content in all three phases increases with decreasing temperature. The phosphorus solubility in α and γ decreases from 2.7 and 1.4 wt pct at 1000°C to 0.25 and 0.08 wt pct at 550°C. The addition of phosphorus to binary Fe-Ni greatly affects the α/α + γ and γ/α + γ boundaries below 900°C. It stabilizes the α phase by increasing the solubility of nickel (α/α +γ boundary) and above 700°C, it decreases the stability field of the γ phase by decreasing the solubility of nickel(@#@ γ/α + γ boundary). However below 700°C, phosphorus reverses its role in γ and acts as a γ stabilizer, increasing the nickel solubility range. The addition of phosphorus to Fe-Ni caused significant changes in the nucleation and growth processes. Phosphorus contents of 0.1 wt pct or more allow the direct precipitation ofa from the parent γ phase by the reaction γ ⇌ α + γ. The growth rate of the α phase is substantially higher than that predicted from the binary diffusion coefficients.

Ternary Phase Equilibria at 450 °C in the Zn-Fe-P System

Experimental determination of phase diagram in the Zn-Fe binary system

Phase equilibria in the Fe-Ti-Zr system at 1023 K

Phase Equilibria in the Ni-Sn-Zn System at 500°C

The ternary phase diagram, Fe-Ni-P

Experimental Study of High Temperature Phase Equilibria in the Iron-Rich Part of the Fe-P and Fe-C-P Systems

Phase equilibria in the Fe–Nb–Zr ternary system at 1,200 °C

Phase Equilibria In The Fe-Nb-Zr Ternary System At 1,200 A Degrees C

Experimental study of the phase relations in the Fe–Cr–Si ternary system at 700°C

Thermodynamic properties and phase equilibria in the Fe–P system

Nonequilibrium solidification of Fe-P alloys

Isothermal Section of Ternary Sn-Zn-Ni Phase Equilibria at 250 °C

Phase equilibria of the Co-Ni-Zr system at 1198 K

Phase Equilibria of the Ternary Ni-Cr-Zr System and Interfacial Reactions in the Ni-Cr/Zr Couples

Thermodynamic Evaluation of the Fe-Zn Binary System with Reference to the Latest Experimental Phase Diagram

Experimental Determination of the Phase Equilibrium in the Mg–Cu–Ca Ternary System at 350 °C

Modeling of temperature-concentration ranges of phase stability and liquidus surface in the ternary Fe–P–C system and phase composition experimental study

Experimental determination of the phase equilibria of the Mg–Nd–Zn system at 320°C

Experimental Study on Phase Relationships in the Co-rich Portion of the Co–Ti–Zr System

Phase Equilibria of the Sn–Zn–Cu Ternary System

The Co–Ni–Zr Phase Diagram in the Zr–ZrCo–ZrNi Region I. Phase Equilibria in the Zr–ZrCo–ZrNi System at Subsolidus Temperature, 900°C, and 800°C