Abstract:Porous silicon carbide/silicon nitride (SiC/Si3N4) composite ceramics with flexural strength of 78 MPa, fracture toughness of 1.68 MPa m1/2, and porosity up to 63% were obtained by gel casting and two-step sintering using commercial phenolic resin as carbon source. Thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), X-ray diffraction (XRD), transmission electron microscopy (TEM), and three-point bending methods were employed to characterize and analyze the microstructure and basic mechanical performance of the porous ceramics. The polymer was proved to be an effective source that could provide free carbon for fabrication of the SiC nanoparticles by in situ reaction with Si3N4 and SiO2. Sizes of the formed SiC particles were in the range of 50–300 nm. Low green density, significant weight loss, and little shrinkage led to high porosity. High aspect ratio of β-Si3N4, uniform porous distribution, and formation of proper amount of SiC particulates were the main reasons for good mechanical performance. However, only a limited amount of polymer additions had these beneficial effects. Excessive additions could cause agglomeration for residual carbon and inborn SiC, hence becoming fatal flaws for the materials.

Investigation on gel casting preparation of porous Si3N 4 ceramics through orthogonal experimental design

Investigation on Gel Casting Preparation of Porous Si3N4 Ceramics Through Orthogonal Experimental Design

Investigation of flexural strength and porosity of porous Si 3N4 ceramics through orthogonal experimental design

Investigation of Gel Casting Preparation of Micro-Porous Si_3N_4 Ceramics

Preparation and Properties of Micro porous Si3N4 Ceramics by Gelcasting

Gelcasting Preparation of Porous Silicon Nitride Ceramics by Adjusting the Content of Monomers

Porous Si3N4 Ceramics Prepared by TBA-based Gel-casting

Neural Network Modeling and Analysis of Gel Casting Preparation of Porous Si3N4 Ceramics

Novel porous Si3N4 ceramics prepared by aqueous gelcasting using Si3N4 poly-hollow microspheres as pore-forming agent

Effect of Different Ratios Between Monomer and Cross-linker on Properties of Gel-Cast Porous Silicon Nitride

PREPARATION OF POROUS Si_3N_4 NANOCOMPOSITES BY GELCASTING

Study on the Process of Si3N4 Ceramic with High Properties by Gel-casting

Fabrication of porous Si 3 N 4 ceramics through a novel gelcasting method

Preparation of in-situ synthesized SiC particles reinforced highly porous Si3N4 ceramics by gel-casting

Preparation of <i>In Situ</i> Synthesized SiC Particles Reinforced Highly Porous Si<sub>3</sub>N<sub>4</sub> Ceramics by Gel-Casting

Processing, Microstructures and Mechanical Properties of Aqueous Gelcasted and Solid-State-Sintered Porous Sic Ceramics

Preparation of porous Si 3 N 4 ceramics via tailoring solid loading of Si 3 N 4 slurry and Si 3 N 4 poly-hollow microsphere content

Influence of fabricated process on mechanical properties of porous SiC-particle/ Si3N4 composites

Microstructure and Properties of Porous Si3N4 Ceramics Fabricated by Gelcasting

PREPARING Si3N4 CERAMICS WITH HIGH PERFORMANCES BY GELCASTING (I)INFLUENCE OF COATING Si3N4 POWDER ON MECHANICAL PROPERTIES OF THE MATERIAL

Gel casting and properties of porous silicon carbide/silicon nitride composite ceramics