Abstract:SiC fibers are widely used in composites exposed to high temperature oxidizing environments. The present study compares the oxidation behavior of SiC fibers and the associated changes in tensile strength upon their exposure to dry air and steam for up to 50 hours at temperatures from 950°C to 1350°C. In both cases, the scale thickness and oxide microstructure were analyzed by scanning electron microscopy. When the SiC fibers were oxidized in air, a crack-free amorphous oxide layer formed at temperatures up to 1200°C, whereas a cracked, crystallized oxide layer was found at 1350°C. By contrast under steam environment, a crystalline oxide forms at 950°C for oxidation times longer than 30 h. In both environments, the fiber strength decreased with increasing exposure time and temperature, the degradation being faster after oxidation in steam compared to dry air. This appears to relate to residual stress in the oxide scale and a reduction in the cross section of the load-bearing unoxidized SiC. An increase in defect size may also contribute to the loss of strength. The oxide scale follows parabolic growth kinetics in both dry air and in steam from 950°C to 1350°C, except at 1350°C for over 30 hours. The oxidation rate in steam is faster than that in dry air, with activation energies of 79.8±1.4 kJ/mol in steam and 153.6±3.4 kJ/mol in air, respectively. This work is relevant to the application of SiC fibers and SiC fiber reinforced composites in air and steam environments at high temperature.

Failure Behavior of C/C Composites with SiC Coating under Stress in Oxidizing Environment

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

Stress‐Oxidation Behavior of a Carbon/Silicon Carbide Composite in a High‐Temperature Combustion Environment

Effect of Oxidation Time on Fracture Behavior of C/SiC Composites at 800 °C in Air

High-Temperature Fatigue Degradation Behaviors of a 3D Braided C/SiC with a Thin Interlayer in Different Dry Oxygen Atmospheres

Effect of oxidation on internal friction behavior of C/SiC composites

High-temperature tensile behavior of 3D SiC/SiC composites

Oxidation behaviors of carbon fiber reinforced multilayer SiC-Si3N4 matrix composites

Oxidation and mechanical properties of SiC fibers after high temperature exposure in air and steam

Influence of Oxidation Damages on Mechanical Properties of SiC/SiC Composite Using Domestic Hi-Nicalon Type SiC Fibers

Oxidation behavior of 3D SiCf/SiBCN composites at 800–1200 °C

Oxidation Kinetics and Its Impact on the Strength of Carbon Short Fiber Reinforced C/SiC Ceramics

Oxidation Behavior of SiC/SiC Composites in Air at High Temperature

Erosion Behavior of C/SiC Composites in Atomic Oxygen

The Degradation Behavior of C/Sic Composites in Complex Environment

Oxidation protection and behavior of C/C composites with an in situ SiC nanowire-SiC-Si/SiC-Si coating

Mechanical and Oxidation Properties of C/SiC Corrugated Lattice Core Composite Sandwich Panels

Mechanical properties and microstructure evolution of KD‐SA SiCf/BN/SiC CMCs oxidized at different temperatures

Non-Destruction Evaluation Method for Long-Term Oxidation Behavior of SiC/SiC Composites with Different Preforms in Wet Oxygen

Oxidation behavior of 3D Hi–Nicalon/SiC composite

Comparison of Oxidation Behaviors of 3D C/PyC/SiC and SiC/PyC/SiC Composites in an O2-Ar Atmosphere