Characterization of microstructures of 2.25Cr-1Mo-0.25V steel after quenching and tempering

Yong T. Zhong,Jiaqiang Gao,HanQian Zhang,Jinfu Li
2008-01-01
Abstract:Quenching and tempering have been carried out on a hot-rolled low alloy 2.25Cr-1Mo-0.25V Steel heavy plate with thickness of 20 mm. It was observed that the quenched steel had a granular bainite microstructure which is composed of upper bainitic ferrite lath with high density dislocations and M-A islands decorating at lath or grain boundaries. When the quenched steel was tempered for 5 hours, a cellular or sub-grain structure developed and established with a large decrease in dislocation density. The M 7C 3 and MC precipitates were identified and characterized by using transmission electron microscope (TEM) and X-ray diffraction (XRD).