Microstructures of 3%C-Cu Composite Powders Prepared by Mechanical Milling

金永平,郭斌,王尔德

DOI: https://doi.org/10.3969/j.issn.1005-0299.2008.05.028

IF: 1.8

2008-01-01

Materials Science and Technology

Abstract:To obtain C-Cu composite powders with excellent microstructures,which are beneficial to such subsequent processes as pressing,sintering and extrusion,3%C-Cu(mass percent) composite powders were prepared by mechanical milling.Their microstructures dependent on milling time were investigated with the scanning electron microscopy(SEM),back-scattered electron images and X-ray diffraction(XRD).The results show that by increasing the milling time,the particle shape of Cu changes from dentritic to laminal,then to nubby and to near-spherical finally.The diffraction peak of graphite disappears after mechanical milling for 2 h.The microstrain of Cu in composite powders increases while lengthening the milling time.The grain size of Cu in composite powders is about 20 nm after milling for 3 h,which confirms that the grain can be refined effectively with this technique.