Abstract:Radial forging was introduced to the strain-induced step in the strain-induced melt activation process to prepare high-quality semi-solid A356.2 billet for the high solid fraction compression. Then, the deformation behaviour and microstructures at different compression velocities, temperatures and deformation zones were investigated. The results showed that radial forging can induce enough strain at 60% reduction of area to prepare ideal semi-solid microstructure. The microstructure had no obvious improvement at 75% reduction of area because the distortion energy may be saturated at 60%. During compression tests, the flow stress was sensitive to compression velocity ( Vc) but was insensitive to holding temperature ( Th), and it obeyed the power law [Formula: see text]. The average strain rate sensitivity was 0.2757, and the average apparent activation energy was 254.5 kJ/mol. The compression sample can be divided into hard deformation zone, transition deformation zone, severe deformation zone and free deformation zone. Different zones had different predominant deformation mechanisms which not only affected the morphology of the grains but also codetermined the flow stress. With increasing Vcand Th, the average particle size was increased from hard deformation zone, reached the maximum at severe deformation zone and then decreased at free deformation zone, while the opposite was the case for shape factor. At each deformation zone, the average particle size was increased while the shape factor was decreased with the increasing Vcbecause higher Vccaused more grains to merge into larger and more irregular grains, while the opposite was the case for the increasing Thbecause higher Thgenerated more liquid which helped to isolate the contacted particles and improve their spheroidization degree.

Mechanical Analysis of Semi-Solid Metals Shear Deformation During Compression

Unexpected Dynamic Recrystallization Behavior of Ti-7Cu Alloy in Semi-Solid State

Deformation Characteristics and Constitutive Equations for the Semi-Solid Isothermal Compression of Cold Radial Forged 6063 Aluminium Alloy

Deformation Behavior of Aluminum Alloy during Semi-Solid Compression

Mechanical Behavior of Processed AZ91D by Equal Channel Angular Extrusion during Semi-Solid Isothermal Compression

Semi-solid compression of 2A14 alloy with high solid fraction: rheology, constitutive equation and microstructure

Experimental study on semi-solid micro-compression of ZL101 alloy

Mechanical Behavior and Microstructure During Compression of Semi-Solid ZK60-RE Magnesium Alloy at High Solid Content

Deformation Behaviour and Microstructures of Semi-Solid A356.2 Alloy Prepared by Radial Forging Process During High Solid Fraction Compression

Numerical Analysis of Semi-Solid Die-Casting Automobile Part Based on the Thermo-Visco-Plastic Constitutive Relation

Deformation Behavior of Semi-Solid Zn–Al Alloy Filler Metal During Compression

Mechanical behaviour of Al/Al2O3 composite in pseudo-semi-solid state during isothermal compression

Deformation Mechanism of Compression of 2024 Al Alloy in Semi-Solid State

Effects of Compression Parameters on Deformation Behaviors of Semi-Solid ZA27 Alloys

Mechanical Behavior of Al–Zn–Mg–Cu Alloy under Tension in Semi-Solid State

Microstructure of semi-solid AZ91D magnesium alloy after hot compression

Numerical Simulation of 6061 Aluminum Alloys during the Semi-Solid Backward Extrusion

Establishment of macro-micro constitutive model and deformation mechanism of semi-solid Al6061

Investigation of Semi-Solid Aluminum Alloy Filling-Plastic Flowing in Thixoforging

Al/Al2O3 composite mechanical behaviour of compression in pseudo-semi-solid sate

Viscosity Estimation of Semi-Solid Alloys Based on Thermal Simulation Compression Tests