Microstructure and mechanical properties of extrusion ZC61 alloys under different dynamic compression loading directions
Zhi Wang,Bingyi Liu,Shouben Huang,Feng Wang,Le Zhou,Pingli Mao,Zheng Liu
DOI: https://doi.org/10.1016/j.mtcomm.2021.103086
IF: 3.8
2022-03-01
Materials Today Communications
Abstract:The dynamic mechanical properties and microstructure of Mg-5.9Zn-0.9Cu-0.4Zr (ZC61) alloy are systematically investigated at strain rate of 1100–2200 s−1, which is manufactured by severe plastic deformation (SPD) processes, i.e. combines traditional hot extrusion with equal channel angular pressing. The microstructural observation reveals that fine equiaxed grains are formed after the hot extrusion-shear process, and the average size of extrusion direction (ED) and extrusion radial direction (ERD) is found to be 41 µm and 32 µm, respectively. The dynamic compression curves exhibit that the peak flow stress improves with increasing strain rate, which shows a positive strain rate enhancement effects. At 2200 s−1 strain rate, the ultimate compression strength of alloy along ED and ERD is found to be 581 MPa and 530 MPa, respectively. During dynamic compression, for ED sample, the {10 1 ̅ 2} extension twinning is observed to be the major plastic deformation mechanism, and the fracture surface exhibits brittle rupture and local melting. Whereas, for ERD sample, the {10 1 ̅ 2} extension twinning and {10 1 ̅ 1 }-{10 1 ̅ 2} secondary twinning (37.5° < 11 2 ̅ 0 >) are found to be dominant deformation mechanisms, and the fracture mode is mainly brittle rupture.
materials science, multidisciplinary