Abstract:Soaking time and loading rate are the two important process parameters for semi-solid powder forming, which are next only to powder temperature. However, there have been few investigations on the influence of soaking time and loading rate on the semi-solid compression of porous material, which is an effective method for studying the deformation characteristics of semi-solid materials and is widely used to optimize the semi-solid forming processes. Therefore, the microstructures, grain size and shape factor, liquid fraction, relative densities and stress–strain curves of Al-4Cu-Mg alloy with a porosity of 30% compacted at different soaking time and loading rates were measured, and the strain rate sensitivity coefficient, the relationship between peak stresses and strain rates, and the processing map were calculated and analyzed. The results indicate that as the soaking time increases, the particle grows and the liquid fraction increases slightly, and the liquid distribution changes from dots in grains to concentrating on grain boundaries in powders, making the relative density increase basically and the peak stress decrease firstly and then increase slowly. Thus, the most suitable soaking time for semi-solid compression is 2 to 5 min. With the loading rate increasing, the particle size reduces first and then increases, the relative density decreases, while the peak stress basically raises, combining the action of powder breakage, grain coarsening and liquid flowing. The peak stress basically has a power relationship with the strain rate, and the processing map can be used to analyze porous semi-solid materials, which are verified to be consistent with the experimental results. Therefore, the optimal semi-solid forming parameters of Al-4Cu-Mg alloy powders are at a deformation rate ranging from 0.6 to 6 mm/s and at a temperature of 860 to 873 K.

Deformation Behavior of Aluminum Alloy during Semi-Solid Compression

Unexpected Dynamic Recrystallization Behavior of Ti-7Cu Alloy in Semi-Solid State

Technological Optimization of Aluminum Alloy Prepared by Semi-solid Method

Investigation on the compression properties of semi-solid Be-Al alloy

Deformation Characteristics and Constitutive Equations for the Semi-Solid Isothermal Compression of Cold Radial Forged 6063 Aluminium Alloy

Effects of pre-deformation on microstructure and mechanical properties of semi-solid 7075 alloy

Semi-solid compression of 2A14 alloy with high solid fraction: rheology, constitutive equation and microstructure

Effects of Heating Rates on Microstructural Evolution of Hot Extruded 7075 Aluminum Alloy in the Semi-Solid State and Thixotropic Deformation Behavior

EFFECTS OF DEFORMATION ON THE MICROSTRUCTURE AND PROPERTIES OF 6082 ALUMINUM ALLOY

Research on the Constitutive Equation of 6061 Aluminum Alloys in the Hot Compressive Deformation

Compressive Rheological Behavior and Microstructure Evolution of a Semi-Solid CuSn10P1 Alloy at Medium Temperature and Low Strain

Influence of Soaking Time and Loading Rate on Semi-solid Compression of Porous Al-4Cu-Mg Alloy

Establishment of macro-micro constitutive model and deformation mechanism of semi-solid Al6061

EFFECT OF AlSi7Mg ALLOY SLURRY INITIAL MICROSTRUCTURE IN THE SOLID-LIQUID ZONE ON THIXOTROPIC DEFORMATION

Hot Deformation Behavior and Microstructure Evolution of High-Strength Al-Zn-Mg-Cu Alloy

Comprehensive study of hot compression behaviors and microstructure evolution of solutionized 6082 aluminum alloy extruded bar

Numerical Simulation of 6061 Aluminum Alloys during the Semi-Solid Backward Extrusion

Hot Deformation Behavior of 2026 Aluminum Alloy During Compression at Elevated Temperature

Microstructure of semi-solid AZ91D magnesium alloy after hot compression

Microstructure characteristics and strengthening mechanism of semisolid CuSn10P1 alloys

Microstructure and high temperature tensile properties of Al–Si–Cu–Mn–Fe alloys prepared by semi-solid thixoforming