Abstract:This study investigates the effects of boron nitride (BN) coating characteristics on the subsurface oxidation behavior of SiC/SiC composites in high‐temperature, water‐rich environments. Three types of coatings were examined: a crystalline stoichiometric BN, an amorphous BN, and a Si‐doped amorphous BN, the latter two containing 5–10 at% of oxygen and carbon. High‐resolution imaging and chemical analysis techniques were used to probe microstructural changes after oxidation at 1000°C for 1 or 12 h in flowing 20 vol% H2O, focusing on effects of coating thickness. Complementary chemical thermodynamic calculations and models for reaction‐ and transport‐controlled recession were used to interpret the experimental findings. Crystalline BN coatings produce open recession channels without forming borosilicate glass, a consequence of carbothermal reduction arising from C/CO produced through concomitant SiC oxidation. The combination of active oxidation and the relatively thick coatings in this system (ca. 1 μm) leads to a recession rate controlled by the intrinsic BN volatilization rate rather than the rate of gas transport. In contrast, amorphous coatings, both undoped and Si‐doped, readily oxidize to form borosilicate glasses that replace the BN. Broadly, the recession lengths increase with coating thickness. In the early stages, while the glass is boria‐rich and thus permeable to environmental oxidants, recession is controlled by the BN oxidation rate. As boria volatilizes, the silica concentration in the glass increases, eventually reaching the saturation limit and precipitating solid silica on the internal surfaces, essentially arresting further recession.

Preparation of BN Coating on Quartz Fibers by a Low-temperature Reaction

Preparation and characterization of t-BN coatings on the surface of carbon fibers

Dielectric Barrier Discharge Assisted Chemical Vapor Deposition of Boron Nitride Phosphide Films on A Quartz Substrate

Preparation of Boron Nitride Nanosheet-Coated Carbon Fibres and Their Enhanced Antioxidant and Microwave-Absorbing Properties

Nearly stoichiometric BN fiber with high crystallinity achieved by boron trichloride assisted curing process

BN Films Deposited by HFPECVD and the Mechanism of the Process

Microstructures and properties of polymer-derived hexagonal boron nitride fibers with initial gradient oxygen contents

Synthesis and Characterization of Nanocrystalline Boron-Nitride Thin Films by Ion Milling and Thermal Treatment for Tribological Coatings: An Approach to Quantifying the Growth Dynamic Process

Liquid-phase deposition of Al2O3 coating on quartz fiber for enhanced strength at elevated temperature

Nitriding Process and Growth Mechanism of Boron Nitride Whiskers

Optimization and kinetics of electroless Ni–P–B plating of quartz optical fiber

Boron Nitride Phosphide Thin Films Grown on Quartz Substrate by Hot-Filament and Plasma-Assisted Chemical Vapor Deposition

Surface-diffusion mechanism for synthesis of substrate-free and catalyst-free boron nitride nanosheets

Pressureless consolidation of boron nitride fiber ceramics via a chemical bonding approach

Characterization of boron nitride nanosheets synthesized by boron-ammonia reaction

Preparation of Thin-Layered Hexagonal Boron Nitride Nanosheet with Oxygen Doping

Insight into the evolution process from novel polyborazine precursor PPMAB to inorganic BN fiber

The effect of deposition temperature of BN interphase on the tensile properties of SiC fibers

Preparation of Boron Nitride-Coated Carbon Fibers and Synergistic Improvement of Thermal Conductivity in Their Polypropylene-Matrix Composites

Influence of BN microstructure on oxidation of SiC/BN/SiC composites

Boron carbide nanowires with uniform CNx coatings