Microstructure Transformation During Homogenization Treatment in As-Cast GH742 Alloy

潘晓林,孙文儒,杨树林,李战,郭守仁,杨洪才,胡壮麒

DOI: https://doi.org/10.3321/j.issn:1005-3093.2008.06.018

2008-01-01

Abstract:The precipitation of as-cast GH742 alloy is complicated and the dendritic segregation is severe.Niobium and titanium are segregated to the interdendritic region and enriched in the precipitates such as MC carbide,Laves phase,δphase,(γ+γ') eutectic.The melting temperature of as-cast GH742 alloy is 1160℃determined by differential thermal analysis and metallography,while the soluble tempera- tures ofγ'phase,(γ+γ') eutectic,MC carbide,Laves phase,δphase,Ni_5Ce phase and RE-O-S phase were determined by different homogenization treatments.In order to obtain uniform austenitic microstructure, a two-step homogenization treatment via low temperature pretreatment followed by high temperature dif- fusion is established due to the melting of RE-O-S phase at 1120℃,which broadens the window of the homogenization temperature and increases the annealing temperature.The diffusion coefficient of niobium is much smaller than that of titanium,which requires more time to be absolutely homogenized.