Abstract:The precipitate dissolution and grain growth during the solution treatment of Ce‐containing 15Cr–22Ni–1Nb steel are investigated. The phase transformation behavior of the Laves phase during hot forging and solution treatment is found and proved. The variation coefficient and 2σ principle in statistics are introduced to quantitatively characterize the abnormal grain growth. The established mathematical model of grain growth can be well applied to predict the average size of austenite grains in the steel after solution treatment. The precipitate dissolution and grain growth during the solution treatment of a newly developed Ce‐containing 15Cr–22Ni–1Nb steel are investigated. The dissolution of eutectic NbC is the result of the elements diffusion along the concentration gradients, and honeycomb (Fe,Cr,Ni,Si)2(Nb,Mo) Laves phase transforms into a more stable Mo2C‐type M2C carbide. As the cerium content is increased from 0 to 0.0630 mass%, the area fraction of eutectic precipitates in forged and solution‐treated 15Cr–22Ni steel is decreased first and then increased. For the steel with 0.0055 mass% cerium content, the substantial reduction in the area fraction of precipitates during hot forging and solution treatment is ascribed to the severe abnormal grain growth. In the case of 15Cr–22Ni steel with 0.0019 and 0.0630 mass% cerium content, the average size of austenite grains after solution treatment is reduced, the multipeak development of grain size distribution is restrained, the range of grain size distribution is narrowed, and the variation coefficient of grain growth, the critical size of abnormally grown grain, and the proportion of abnormally grown grain are all decreased. The variation coefficient of grain growth and the critical size of abnormally grown grain in the steel are increased as the solution time is extended, whereas the proportion of abnormally grown grain presents a general trend of reduction. The established mathematical model of grain growth in the paper can be well applied to predict and control the average size of austenite grains in 15Cr–22Ni steel after solution treatment.

Effect of homogenization treatment on microstructure and eutectic precipitates in Ce‐containing 15Cr–22Ni–1Nb austenitic heat‐resistant stainless steel

Precipitate Dissolution and Grain Growth during Solution Treatment of Ce‐Containing 15Cr–22Ni–1Nb Austenitic Heat‐Resistant Steel

Microstructure Evolution and Homogenization Kinetics of 15Cr–30Ni–Fe Heat‐Resistant Alloy

Effect of solution treatment on microstructure and mechanical properties of Cr18Ni10Cu3NbN austenite stainless steel

Effect of homogenization temperature on microstructure and mechanical properties of low-carbon high-boron cast steel

The influence of homogenization on the microstructure and high-temperature mechanical properties of ERNiCrMo-3 alloy

Influence of Borides Dissolution During the Homogenization Treatment on the Mechanical Properties and Fracture Behavior of Austenitic Stainless Steel Brazed Joints

The Effect of Homogenization Heat Treatment on 316L Stainless Steel Cast Billet

Solidification Segregation Behavior and Homogenization Process of a Difficult-to-Deform Superalloy Used at 850 °C

Influence of cerium treatment on inclusion modification and as-cast microstructure of high-strength low-alloy steel

Effect of Ce Content on Microstructure-Toughness Relationship in the Simulated Coarse-Grained Heat-Affected Zone of High-Strength Low-Alloy Steels

Effect of Homogenization Treatment on Microstructure of 6063 Alloy

Eutectic precipitates and microstructure of electroslag remelted 15Cr–22Ni austenitic heat-resistant steel with varying Nb contents

Effect of homogenization on precipitation behavior and strengthening of 17-4PH stainless steel fabricated using laser powder bed fusion

Microstructure Evolution and Mechanical Properties of Homogenizing Treated Fully Lamellar Ti-46 Al-0 . 5 W0 . 5 Si Alloy

Influence of B addition on the Mo diffusion-controlled eutectic dissolution process during homogenization of super austenitic stainless steel S31254

Optimization of Inclusion and Microstructure of As‐Cast Nonquenched and Tempered Steel F38MnVS with Trace Ce

Homogenization Treatment-Induced Reduction of Brittle Intermetallic Compounds in Ti2alnb/Ti60 Brazed Joints: Effect on Microstructure and Mechanical Properties

The Optimized Homogenization Process of Cast 7Mo Super Austenitic Stainless Steel

Uncovering the effects of Ce and superheat temperature on Fe-rich intermetallic and microporosity formation in aluminum alloy

Precipitate Evolution in 22Cr25NiWCuCo(Nb) Austenitic Heat-Resistant Stainless Steel during Heat Treatment at 1200 °C