Abstract:Electroless nickel composite coatings have the potential for high-temperature tribological applications, and a combination of high wear resistance and low friction factor is one of the desirable solutions but still a tricky problem. The addition of self-lubricating WS2 and hard Si3N4 nanoparticles to the Ni-P coatings is expected to obtain good high-temperature tribological performance. In this work, Ni-P-Si3N4-WS2 composite coatings with various contents of WS2 nanoparticles were prepared using electroless plating and subsequently annealed at 400 °C in an inert atmosphere. The tribological properties of the coatings were evaluated using a ball-on-disc wear instrument at operating temperatures from 25 to 600 °C. The microstructure, chemical composition, and surface morphology of the coatings were characterized by X-ray diffractometry (XRD), energy disperse spectroscopy (EDS), and scanning electron microscopy (SEM). Upon increasing the WS2 dosage in the bath, the WS2 content in the coating increased and the micro-hardness of the as-plated coating increased from 539 to 717 HV. After heat treatment, the coating underwent a crystallization process, and the hardness increased from 878 to 1094 HV. The main wear mechanism of the coating changed from adhesive wear in the as-plated state to abrasive wear in the annealed state. The annealed Ni-P-Si3N4-WS2 coating with a WS2 dosage of 2.5 g/L in the bath exhibited excellent mechanical properties, with a hardness of 10.9 GPa, a friction coefficient of ~0.51, and a wear rate of 8.4 × 10−15 m3N−1×m−1 at room temperature, and maintained optimal performance at high temperatures. At operating temperatures of 200, 400, and 600 °C, the form of wear was adhesive wear for coatings with a WS2 dosage < 1.5 g/L and abrasive wear for coatings with a WS2 dosage ≥ 1.5 g/L. The synergism of WS2 and Si3N4 particles refined the grains of the Ni-P matrix in as-plated coatings and obviously reduced the friction coefficient of friction pairs in annealed coatings at all operating temperatures.

Tribological Properties of Plasma Sprayed Nano-Sicp/Fes Composite Coatings

Characterization and tribological properties of plasma sprayed FeS solid lubrication coatings

Studying on the Tribological Properties of Self- Lubricate Nano FeS Coating Deposited by Plasma Spraying

Microstructure and properties of plasma sprayed copper-matrix composite coatings with Ti3SiC2 addition

Comparison of the tribological properties of an ion sulfurized coating and a plasma sprayed FeS coating

Effect of MoS2 Content on Microstructure and Properties of Supersonic Plasma Sprayed Fe-based Composite Coatings

A Comparison of the Tribological Properties of SiC Coatings Prepared via Atmospheric Plasma Spraying and Chemical Vapor Deposition for Carbon/Carbon Composites

Microstructures and Anti-friction Property of Sprayed Sulfide Coating

Microstructure and tribological properties of Al-30Si-5Cu composite coating reinforced with ceramic phases synthesized in situ by plasma spraying

The Iron Sulfide Coatings Prepared by Plasma Spraying and Their Friction-Reduction Performance

Plasma sprayed TiC–Ti5Si3–Ti3SiC2 composite coatings from Ti–SiC-graphite powders with different SiC particle size

Microstructure evolution and mechanical properties of reactive plasma sprayed Ti3SiC2–Ti5Si3–TiC composite coatings

Tribological behavior of sol-gel FeS coating

Wear Properties of Plasma Transferred Arc Fe-based Coatings Reinforced by Spherical WC Particles

Study on the Tribological Properties of Carbon Fabric/Polyimide Composites Filled with SiC Nanoparticles

Tribological Behavior of Plasma Sprayed Al–Cu–Fe + Sn Quasicrystalline Composite Coatings

Fabrication of Ni60–SiC Coating on Carbon Steel for Improving Friction, Corrosion Properties

Friction and wear properties of CrSiCN coatings with low carbon content as sliding against SiC and steel balls in water

High Temperature Tribological Behavior of Electroless Plating Ni-P-Si3N4-WS2 Composite Coatings

Tribological Property of Plasma-Sprayed Al2O3-13wt%TiO2 Coatings Onto Resin-Based Composites

Microstructure and Tribological Behaviour of Super-Hard Ti–Si–C–N Nanocomposite Coatings Deposited by Plasma Enhanced Chemical Vapour Deposition