Microstructure and tribological properties of Al-30Si-5Cu composite coating reinforced with ceramic phases synthesized in situ by plasma spraying
Jiahao Zhang,Binguo Fu,Yanfei Jiang,Tianshun Dong,Guolu Li
DOI: https://doi.org/10.1016/j.surfcoat.2024.130946
IF: 4.865
2024-05-29
Surface and Coatings Technology
Abstract:For improving the wear resistance of Al-30Si-5Cu coating, in this study, the composite coating in-situ synthesized TiC-TiN-TiN 0.8 C 0.2 /Al-30Si-5Cu (TiCN/Al-30Si-5Cu) was prepared used TiH 2 -graphite aggregates as raw materials and plasma spraying technology. The effect of in-situ synthesized ceramic reinforcements on the coating was researched in detail. The results showed that during the plasma spraying process, TiH 2 decomposed and chemically reacted with graphite to form TiC. Additionally, some Ti also reacted with N 2 and O 2 in the air to form TiN and TiO 2 . The phases composition of TiCN/Al-30Si-5Cu composite coating were α-Al, β-Si, θ-Al 2 Cu, β-Ti, TiC, TiN, TiN 0.8 C 0.2 , TiO 2 , as well as amorphous CN X and residual graphite. The TiC-dominated ceramic phases and β-Si were uniformly distributed in the coating, which were tightly bound to the α-Al matrix. Because of the exceptionally rapid cooling rate during the coating preparation, a minor amount of submicron Si particles were also generated. The microhardness, elasticity modulus, and fracture toughness of TiCN/Al-30Si-5Cu composite coating appeared improvements compared to those of Al-30Si-5Cu coating. The TiCN/Al-30Si-5Cu composite coating exhibited smoother friction coefficient curve, along with lower friction coefficient and wear volume in comparison to the Al-30Si-5Cu coating. This suggested that the ceramic reinforcing phases in-situ synthesized led to a notable advancement in the wear resistance of the TiCN/Al-30Si-5Cu composite coating. The wear resistance of TiCN/Al-30Si-5Cu composite coating demonstrated an increasement of 78.3 % over the substrate and 28.2 % over the Al-30Si-5Cu coating. Under the dry friction test conditions outlined in this study, the wear mechanism of the TiCN/Al-30Si-5Cu composite coating included abrasive wear and fatigue wear, coupling with a minimal amount of oxidative wear.
physics, applied,materials science, coatings & films