Abstract:In order to improve safety and combustion properties of RDX-CMDB propellant, lead stearate was used to coat RDX by means of chemical precipitation method, then the RDX/lead stearate composite particles were prepared. The samples were characterized by using SEM (scanning electron microscope) and XPS (X-ray photoelectron spectrometry). The mechanical sensitivity of RDX samples before and after coating was measured and contrasted. Meanwhile, thermal decomposition catalytic properties of RDX-CMDB propellant before and after coating were investigated respectively by DSC. The results show that the mechanical sensitivity of RDX coated by lead stearate decreases significantly; the impact sensitivity characteristic height (H50) increases by 17.6 cm, and the friction explosion probability decreases by 60%. Compared with the propellant containing uncoated RDX, the exothermic peak temperature of NC/NG with RDX/lead stearate composite particles decreases by about 3.7°C, and the total exothermic quantity of the propellant increases.

Preparation and characterization of RDX/lead stearate composite particles