Enhancing RDX Thermal Decomposition in Al@RDX Composites with Co Transition Metal Interfacial Layer

Su-Lan Yang,Kan Xie,Jing Wang,Bingchen An,Bin Tian,Hongqi Nie,Jie-Yao Lyu,Qi-Long Yan

DOI: https://doi.org/10.3390/aerospace11010081

IF: 2.66

2024-01-17

Aerospace

Abstract:In this study, an Al/Co@RDX composite was meticulously prepared through a combination of planetary high-energy ball-milling and a spray-drying technique. The thermal reactivity of these Al/Co@RDX composites was comprehensively investigated and compared using the TG/DSC technique. It is shown that the initial decomposition temperature of RDX in the DSC curve was decreased by 26.3 °C in the presence of Al/Co, which could be attributed to the nano-sized Co transition metal catalyzing the decomposition reaction of nitrogen oxides in RDX decomposition products. The decomposition peak temperature of RDX and the heat released by the thermal decomposition of RDX in the Al/Co@RDX composite were decreased by 26.3 °C and increased by 74.5 J·g−1, respectively, in comparison with those of pure RDX. The types of major gaseous products released from Al/Co@RDX were found to be identical to those of pure RDX, encompassing N2O, CH2O, CO2 and HCN. However, the concentrations of those gaseous products for Al/Co@RDX were higher than those observed for pure RDX, which may owe to the fact that the Al/Co composite can interact with the –CH2 and –NO2 within RDX molecules, which leads to the weakening of the C-N and N-N bonds. In addition, the decomposition of RDX in the Al/Co@RDX composite was observed as a one-step process with an apparent activation energy (Ea) of 115.6 kJ·cm−3. The decomposition mechanism of the RDX in the Al/Co@RDX composite was identified to follow the chain scission model (L2), whereas the two-step decomposition physical models observed for pure RDX were found to closely resemble the L2 and autocatalytic models.

engineering, aerospace

What problem does this paper attempt to address?

The paper attempts to address the issue of enhancing the thermal decomposition performance of RDX by introducing a cobalt (Co) transition metal interfacial layer into aluminum (Al) and RDX composites. Specifically, the study aims to:

1. **Lower the initial decomposition temperature of RDX**: By introducing the Co interfacial layer, the study hopes to significantly reduce the initial decomposition temperature of RDX, thereby increasing its thermal reactivity.
2. **Increase the exothermic amount during the thermal decomposition process**: By enhancing the thermal decomposition reaction of RDX, the study aims to increase the amount of heat released during the thermal decomposition process, thereby improving the overall energy release performance of the composite material.
3. **Improve the kinetic behavior of RDX thermal decomposition**: The study hopes to alter the thermal decomposition mechanism of RDX by introducing the Co interfacial layer, transforming it from a two-step decomposition process to a one-step decomposition process, and reducing the apparent activation energy.

The achievement of these goals will help to enhance the combustion performance and energy release efficiency of high-energy composite propellants containing RDX and Al, thus having significant application value in fields such as aerospace.