A New Type of Cu–Al–Ta Shape Memory Alloy with High Martensitic Transformation Temperature
C. P. Wang,Y. Su,S. Y. Yang,Z. Shi,X. J. Liu
DOI: https://doi.org/10.1088/0964-1726/23/2/025018
IF: 4.1
2014-01-01
Smart Materials and Structures
Abstract:In this study, a new type of Cu-Al-Ta (Cu86Al12Ta2 wt%) shape memory alloy with high martensitic transformation temperature is explored. The microstructure, reversible martensitic transformation and shape memory properties are investigated by means of optical microscopy, back-scattered electron, electron probe microanalysis, x-ray diffraction, differential scanning calorimetry and tensile tests. It is proposed that Cu86Al12Ta2 alloy consists of a mixture of primarily beta(1)' martensite and a little gamma(1)' martensite and some different precipitates. The tiny thin-striped Ta-2(Al, Cu)(3) precipitate is predominant in the as-quenched condition, whereas the particle-shaped Cu(Al, Ta) precipitate is dominant after hot-rolling. Additionally, the dendritic-shaped gamma(1)(Cu9Al4) phase begins to appear after hot-rolling, but it disappears when the sample is re-quenched. All studied samples have reversible martensitic transformation temperatures higher than 450 degrees C. The results show that two-step martensitic transformation behavior is observed for Cu86Al12Ta2 alloy in all three different conditions due to the transformations between (beta(1)' + gamma(1)') martensites and the austenite parent phase. The results further show that the recovery ratios are almost 100% when the pre-strains are <= 2.5%, then they gradually decrease with further increase of the pre-strains. The shape memory effects clearly increase as a result of increase of the pre-strains, up to a maximum value of 3.2%.