Microstructure, Martensitic Transformation, Mechanical and Shape Memory Properties of Ni–Co–Mn–In High-Temperature Shape Memory Alloys under Different Heat Treatments

Shuiyuan Yang,Cuiping Wang,Zhan Shi,Jinming Wang,Jinbin Zhang,Yixiong Huang,Xingjun Liu

DOI: https://doi.org/10.1016/j.msea.2015.12.091

IF: 6.044

2015-01-01

Materials Science and Engineering A

Abstract:The microstructure, martensitic transformation behavior, mechanical and shape memory properties of Ni40Co10Mn41+xIn9−x (x=0, 2 and 4) high-temperature shape memory alloys annealed at 900°C for 24h or at 800°C for 2h were investigated, respectively. The tetragonal martensite phase and fcc γ phase are observed in all the studied alloys. The reversible martensitic transformation temperatures of the alloys increase with the increases of the electron concentration and the tetragonality of martensite phase. The amount of γ phase gradually increases with the decrease of In content, and much more γ phase in the alloys annealed at 900°C results in slightly larger compressive fracture strain. Although the alloys with x=0 and 2 have a mass of γ phase, they still exhibit good shape memory properties. The amount of γ phase reaches about 20% in the alloy with x=0 after annealed at 900°C, but a full recovery strain of 3.6% and a two-way shape memory effect of 0.8% can be obtained after two thermomechanical cycles.