Effect of aging at average temperature in β1-phase on the transformation characteristic and structure of martensite in Cu-12.37Al-3.14Mn-0.10Zr alloy

Zhou Li,Mingpu Wang,LingFei Cao,Genying Xu,Yanhui Wang,Ben Xu,HuiYing Zhang

2002-01-01

Abstract:The transformation characteristic and structure changes of martensite of the Cu-12.37 Al-3.14 Mn-0.10 Zr alloy aging at average temperature were studied by means of R-T carve, X-ray diffraction and electron diffraction. It was convinced that the tested alloy has a high properties of aging-resistance at average temperature in the parent phase. It has a good thermoelastic martensite transformation characteristic after aging at 400°C for 96 h in the parent phase, the reversible martensite is up to 90%. The martensite characteristic temperature (Ms) slightly rises for 10-15°C during early aging, and was almost constant during later aging. The quenched martensite has M2H structure, and it transforms gradually into M18R with elongation of the aging time. During aging the γ2-phases precipitate, which causes that the basal body leans Al and the electron concentration falls down. And this leads the rising of the martensite characteristic temperature (Ms) and the change of the martensite structure.