Abstract:Study on the corrosion behavior of reinforcing steel is one of the most significant research topics in the field of corrosion and protection of metals. The scanning microelectrode technique is a powerful tool to study localized corrosion behavior of reinforcing steel in a corrosive solution. In this work, the corrosion behavior of reinforcing steel in a simulated concrete pore solution with Cl - and the inhibition effect of a mixture of NaNO 2 and Na 2 SiO 3 on the steel were studied by the scanning microelectrode technique assisted by polarization curve measurements and surface analyses. Q235 reinforcing steel was used as the tested material. The cylindrical steel specimen with dimension of Æ1.14 cm ´ 0.50 cm was sealed in a PVC holder enveloped with epoxy resin, and only a cross section (1.00 cm 2 ) of the steel served as the working surface. Before experiments, the steel specimen was sequentially polished by silicon carbide sandpaper up to 1500 grit and 0.3 µm Al 2 O 3 powder, and then ultrasonically cleaned in deionized water and ethanol. A saturated Ca(OH) 2 solution was used as the simulated concrete pore (SCP) solution. The simulated polluted concrete pore (SPCP) solution was prepared from SCP solution by adjusting its pH to 11.50 with deionized water and adding 0.05 M NaCl. NaNO 2 and Na 2 SiO 3 with different concentrations as corrosion inhibitors were added to the SPCP solution. The potential distribution on the reinforcing steel surface was measured by a home-built scanning microelectrode measurement system. Ag/AgCl electrodes were used as a scanning microprobe and a micro-reference electrode. Polarization curve measurements were carried out by an Autolab Potentiostat Galvanostat. A three–electrode cell was used with the steel specimen as the working electrode, a saturated calomel electrode (SCE) as the reference electrode and a platinum electrode as the counter electrode. All the measurements were performed at ambient temperature. The results showed that there were no stable large potential peaks on the steel surface in the pure Ca(OH) 2 solution with pH 12.50 or 11.50, indicating that the steel surface was in a passive state and no corrosion took place. For the steel in the SPCP solution with 0.050 M NaCl and pH 11.50, a stable and large local potential peak occurred on its potential map after 20 min immersion. This result indicated that the steel was active and localized corrosion occurred resulting from the Cl - attack. For the SPCP solution with 0.004 M NaNO 2 and 0.001 M Na 2 SiO 3 , there were no stable potential peaks on the potential map of the steel immersed in the solution for 8 h, indicating that no localized corrosion took place. Therefore, the mixture of NaNO 2 with Na 2 SiO could protect the reinforcing steel from corrosion. The polarization curve measurements and surface analyses also confirmed the above results. This work was supported by the National Natural Science Foundation of China (Nos. 21073151, and 21173177).

Study on Localized Corrosion Behavior of Reinforcing Steel by Scanning Microelectrode Technique

Corrosion Behavior of Reinforcing Steel in Simulated Concrete Pore Solutions: A Scanning Micro-Reference Electrode Study

Study on the Corrosion Behavior of Reinforcing Steel by Electrochemical Techniques and Xps

Developing a Novel Expression for Chloride Ion Concentration Threshold in Reinforced Concrete: Integration of Electrochemical Analysis and Time-Dependent Modeling

Study on effect of chloride ions on corrosion behavior of reinforcing steel in simulated polluted concrete pore solutions by scanning micro-reference electrode technique

Study on Corrosion Inhibition of Reinforcing Steel in Simulated Concrete Pore Solutions by Scanning Microelectrode Technique

Study on the corrosion behavior of reinforcing steel in simulated concrete pore solutions using in situ Raman spectroscopy assisted by electrochemical techniques

In-Situ Measurement of Potential Distribution on Surface of Reinforcing Steel in Simulated Concrete Pore Solution

Localized Corrosion Behaviour of Reinforcement Steel in Simulated Concrete Pore Solution

Determination of the Chloride Threshold Concentration for Reinforcing Steel Corrosion Initiation in Simulated Concrete Pore Solution

Effect of pH on the corrosion behavior of reinforcing steel in simulated concrete pore solutions

CORRELATION BETWEEN COMPOSITION OF REINFORCING STEEL SURFACE FILM AND STEEL CORROSION BEHAVIOR IN SIMULATED CONCRETE PORE SOLUTIONS

The Electrochemical Characterization of Rebar Passivation Film in Simulated Concrete Media

Electrochemical and Xps Study on Effect of Cl- on Corrosion Behavior of Reinforcing Steel in Simulated Concrete Pore Solutions

EIS analysis on chloride-induced corrosion behavior of reinforcement steel in simulated carbonated concrete pore solutions

A Self-Balanced Electrochemical Model for Corrosion of Reinforcing Steel Bar in Considering the Micro-Environments in Concrete

EXPERIMENTAL STUDY OF PIEZOMAGNETISM OF PITTING CORROSIONSTEEL BARS UNDER TENSILE FORCE

Influence of Chloride Ions on Corrosion Behavior of Steel Bars in a Simulated Concrete Pore Solution