Abstract:This paper reports the synthesis of semiconductor ZnSe microspheres composed of nanoparticles via a solvothermal route between the organic molecule selenophene (C4H4 Se) and ZnCl2 without adding any surfactant. The ZnSe microspheres were characterized by x-ray diffraction (XRD), Raman spectroscopy, scanning electron microscopy (SEM), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), high resolution transmission electron microscopy (HRTEM), specific surface area measurement, and photoluminescence (PL) spectra. A strong and broad blue PL emission at 443 nm in wavelength (similar to 2.79 eV in photon energy) is attributed to the near-band-edge (NBE) emission of ZnSe, while the 530 nm peak is a defect-related (DL) emission. The photocatalytic activity of the as-prepared ZnSe microspheres was evaluated by photodegradation of methyl orange (MO) dye under ultraviolet (UV) light and visible light irradiation. The degradations of MO reach 94% or 95.1%, close to 100%, in the presence of the as-synthesized ZnSe microspheres or commercial ZnSe powder after 7 or 10 h under UV irradiation, respectively. Meanwhile the degradations of MO reach 94.3% or 60.6% in the presence of the as-synthesized ZnSe microspheres or commercial ZnSe powder after 12 h, respectively. The degradation rate of ZnSe microspheres is twice that of ZnSe commercial powder under UV light irradiation, and three times under visible light irradiation. The degradation process of MO dye on ZnSe microspheres under UV or visible light is also discussed.

Preparation and Properties of ZnSe Microspheres

The synthesis and photocatalytic activity of ZnSe microspheres.

Synthesis Of Monodispersed Znse Quasi-Nanospheres By Hydrocarbon Solvothermal Method

Preparation of Monodisperse Se Colloid Spheres and Se Nanowires Using Na 2 SeSO 3 As Precursor

Preparation and Properties of Nanoparticles ZnS

Preparation of Mesoporous ZnO Microspheres Through a Membrane-Dispersion Microstructured Reactor and a Hydrothermal Treatment

One-Step Hydrothermal Preparation of ZnSe Nanorods and Their Characterization

An Aqueous Approach to ZnSe and CdSe Semiconductor Nanocrystals

Synthesis and Characterization of Zinc Sulfide Hollow Microspheres

Generation And Optical Properties Of Monodisperse Wurtzite-Type Zns Microspheres

ZnSe Semiconductor Hollow Microspheres.

Preparation and Characterization of Silver Coated Hollow SnO2 Sphere with Open Structure

Growth and Characterization of Single-Crystal ZnSe Nanorods Via Surfactant Soft-Template Method

Size- and Shape-Controlled Synthesis of ZnSe Nanocrystals Using SeO2 As Selenium Precursor.

Synthesis and Characterization of Monodisperse CdSe Quantum Dots with Zinc Blende Structure

Synthesis and characterization of ZnSe and ZnSe/ZnS quantum dots for potential biomedical application

Controlled Synthesis and Characterization of Znse Quantum Dots

Facile Route To Zn-Based Ii-Vi Semiconductor Spheres, Hollow Spheres, And Core/Shell Nanocrystals And Their Optical Properties

Synthesis and Characterization of Monodisperse ZnS Nanospheres

Formation of Vesicle-Templated CdSe Hollow Spheres in an Ultrasound-Induced Anionic Surfactant Solution.

Preparation of ZnSe powder by vapor reaction during combustion synthesis