Abstract:In this present study, synthesized zinc ethyl carbamate is thermally decomposed to give wurtzite ZnS nanoparticles. SEM shows polydispersed spherical and cubic structures while EDX reveals approximately a 1 : 1 Zn to S ratio. Tauc's plot give 3.93 eV and 3.42 eV as the band gaps for the nanoparticles synthesized at 300 and 400 °C respectively. This study explores the synthesis of nanoparticles through the thermal decomposition of single‐source precursors, a method gaining popularity due to its low cost, minimal environmental toxicity, rapidity, scalability, and the ability to form nanoparticles with few defects. Zinc ethyl carbamate was synthesized and characterized using 1H NMR and infrared spectroscopy. Its purity was confirmed through microelemental analysis and melting point determination. The melting point of the complex was determined to be 165 °C. The thermogravimetric analyses indicated a one‐step decomposition of zinc ethyl carbamate with a decomposition onset of of 200 °C, yielding a stable ZnS residue. Further thermal decomposition led to the formation of wurtzite phase ZnS nanoparticles, as evidenced by XRD. SEM micrographs displayed mixed spherical, and cubic unevenly sized, polydispersed nanoparticles, while EDX revealed approximately a 1 : 1 Zn to S ratio. Estimated band gap from the Tauc's plot gave 3.93 eV and 3.42 eV for the nanoparticles synthesized at 300 and 400 °C respectively. The wide difference in the band gaps may be as a result of the larger particles observed at 400 °C and the deformations in the sample as observed in the SEM.

Synthesis and Characterization of Zinc Sulfide Hollow Microspheres

Synthesis of Two-Dimensional Micron-Sized Single-Crystalline ZnS Thin Nanosheets and Their Photoluminescence Properties

Synthesis and Characterization of Monodisperse ZnS Nanospheres

Studies of synthesis and optical properties of ZnS nanocrystals

One-pot synthesis of ZnS hollow spheres via a low-temperature, template-free hydrothermal route

Novel CuS Hollow Spheres Fabricated by a Novel Hydrothermal Method

Solvothermal Synthesis of Core–shell ZnO Hollow Microhemispheres

Solventless Synthesis of Zinc Sulphide Nanoparticles from Zinc Bis(diethyldithiocarbamate) as a Single Source Precursor

Preparation of Hollow Cu2ZnSnS4 Spheres via Solvothermal Method

A general and rapid synthesis of metal sulphides hollow spheres that have properties enhanced by salt-assisted aerosol decomposition: a case of ZnS and other multicomponent solid solutions

Alpha-calcium Sulfate Hemihydrate Used As a Water-Soluble Template for the Synthesis of ZnO Hollow Microspheres

Synthesis And Characterization Of Monodisperse Doped Zns Nanospheres With Enhanced Thermal Stability

Controllable Synthesis, Characterization, and Growth Mechanism of Hollow Znxcd1-Xs Spheres Generated by A One-Step Thermal Evaporation Method

Generation And Optical Properties Of Monodisperse Wurtzite-Type Zns Microspheres

Synthesis and Characterization of Hollow Sb2Se3 Nanospheres

From ZnO nanorods to 3D hollow microhemispheres: solvothermal synthesis, photoluminescence and gas sensor properties

Synthesis and Characterization of Monodisperse CdSe Quantum Dots with Zinc Blende Structure

Synthesis of ZnS hollow nanoneedles via the nanoscale Kirkendall effect

The Optical Properties of Nano-particles ZnS

HYDROTHERMAL SYNTHESIS OF DENDRITE-LIKE ZINC SULFIDE CRYSTALS

Synthesis and characterization of ZnS nanowires by AOT micelle-template inducing reaction