Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Crevice Corrosion Behavior of the Steel X70 under Cathodic Polarization

Study of Overprotective-Polarization of Steel Subjected to Cathodic Protection in Unsaturated Soil

Initiation and propagation of pitting and crevice corrosion of hydrogen-containing passive films on X70 micro-alloyed steel

Blunt and penetrating trauma--has anything changed?

STUDY OF THE X70 PIPELINE STEEL CORRODING IN 3.0wt% NaCl SOLUTION USING ELECTROCHEMICAL IMPEDANCESPECTROSCOPY TECHNIQUE

Local electrochemistry of reinforcement steel – Distribution of open circuit and pitting potentials on steels with different surface condition

Effects of cathodic protection potential on microbiologically induced corrosion behavior of X70 steel in a near-neutral pH solution

Analysis of Polarization Curves Characteristics of Rebar in Concrete

Accelerating Effect and Critical Ph Value of Occluded Cell Corrosion Within Pits, Crevices, or Stress Corrosion Cracks

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Passivation and Depassivation of HPB335 Carbon Steel in Simulated Concrete Pore Solution

Investigation of Crevice Corrosion Behavior of HRB355 Steel in 3.5% NaCl solution using Coupled multi-electrode arrays

Electrochemical Investigation of the Corrosion Behavior of API 5L-X65 Carbon Steel in Carbon Dioxide Medium

Properties of Surface Film on X70 Pipeline Steel in CO3^2-／HCO3^- Environment

Properties of Surface Film on XT0 Pipeline Steel in CO2-3/HCO-3 Environment

Effects of mechanical stress and cathodic protection on the performance of a marine organic coating on mild steel

Study of Crevice Corrosion Behavior and Cathodic Protection of Carbon Steel Reinforcement in Concrete

On the Impact of Cathodic Polarization on the Chloride Threshold of Carbon Steel in Alkaline Solutions

Properties of surface film on X70 pipeline steel in CO32-/HCO3- environment

Corrosion Behavior of X70 Pipeline Steel in 3.5% Nacl Solution under the Synergistic Action of Cathodic Protection and Sulfate- reducing Bacteria

Effect of cathodic polarizations on the failure behavior of epoxy coating/low alloy steel systems under high hydrostatic pressure