Abstract:A mixture of titanium isopropoxide, acetic acid and deionized water in a volume ratio of 1: 16: 40 generated a solution containing Ti (IV) polycation species, which was allowed to exchange with alkylammonium ions in the interlayers of the n-decylamine-preswelled titanoniobate. This exchange reaction led to the formation of Ti(IV) polycation-intercalated layered titanoniobate with an interlayer distance of 1.70 nm. The ordered layered structure of the novel material was still retained upon calcination at 623 K. Characterizations of XRD and N-2 adsorption-desorption isotherms indicated that the TiO2-pillared HTiNbO5 (abbreviated to TiO2-HTiNbO5) obtained by calcination at 723 K in air environment was a porous layered materials with an interlayer distance of 0.97 nm and a BET specific surface area of 89 m(2)/g. The vapor phase Beckmann rearrangement reaction of cyclohexanone oxime was studied with TiO2-HTiNbO5 and B2O3/TiO2-HTiNbO5 as catalysts. The cyclohexanone oxime conversion and the selectivity for the formation of e-caprolactam on B2O3/TiO2HTiNbO5 were higher than those on TiO2-HTiNbO5. The B2O3/TiO2-HTiNbO5 catalyst with B2O3 loading mass fraction of 7.31% exhibited a near-100% conversion of the oxime within 4.5 h and a near 90% selectivity for epsilon-caprolactam. FTIR spectra indicated that highly dispersed BO4 species were present in the surface of B2O3/TiO2-HTiNbO5 with a low B2O3 loading; for the B2O3/TiO2-HTiNbO5 samples with a B2O3 loading higher than 7.31%, BO3, species were dominant. BO4 and BO3, species on the surface of TiO2-HTiNbO5 showed synergistic promotion effect for vapor-phase Beckmann rea-rrangement reaction of cyclohexanone oxime.

Preparation of Tio2-Pillared Hnb3o8: Tetrabutyl Titanate Used As A Cheap Titanium Source

Preparation and Characterization of Tio2-Pillared Layered Hnb3o8

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

Modification of the Interlayer in HTiNbO5 and its Physicochemical Characterization

Preparation of TiO_2-pillared HTiNbO_5 and Catalytic Performance in Vapor Phase Beckmann Rearrangement Reaction of Cyclohexanone Oxime

Synthesis Of Titania-Pillared Layered Niobic Acid With A High Specific Surface Area By Using Sol-Intercalation Method

Synthesis and characterization of titania-pillared layered HLaNb2O7 with high specific surface area

Synthesis and Characterization of Porous Chromia-Pillared Layered Titanoniobate

Preparation of A Monodispersed Suspension of Barium Titanate Nanoparticles and Electrophoretic Deposition of Thin Films

Method for preparing CaTi2O4(OH)2 nanolayer

SYNTHESIS OF AL2O3-PILLARED LAYERED TITANONIOBATE

Preparation of Alumina-pillared Layered Titanoniobates with Different Interlayer Distances

Hydrothermal Synthesis of Tetragonal Barium Titanate Nanopowders under Moderate Conditions

Layered oxide precursor strategy for the synthesizing of titanium oxynitrides

Preparation and Properties of Nanostructure Anatase Tio2 Monoliths Using 1-Butyl-3-methylimidazolium Tetrafluoroborate Room-Temperature Ionic Liquids As Template Solvents

Highly Thermostable, Porous, Layered Titanoniobate Pillared by Silica

The Critical Effect of Niobium Doping on the Formation of Mesostructured TiO2 : Single-Crystalline Ordered Mesoporous Nb-TiO2 and Plate-like Nb-TiO2 with Ordered Mesoscale Dimples

Titania Polymorphs Derived from Crystalline Titanium Diboride

Synthesis of TiO$lt;inf$gt;2$lt;/inf$gt; Nanoparticles Using Hydrogel As Template and TiO$lt;inf$gt;2$lt;/inf$gt; Microspheres Using Microfluidic

Synthesis and characterization of TiO2-pillared microporous manganese oxide

Preparation of Bionic Structure TiO2 Using Napkin As Template and Its Photocatalytic Performance