Abstract:A water-based route has been demonstrated for synthesizing ZnSe and Cd-doped ZnSe (ZnSe(ZnxCd1-xSe, 0 < x < 1) quantum dots (QDs) that have tunable and narrow photo luminescence (PL) peaks from the ultraviolet A (UVA) to the blue range (350-490 nm) with full-width at half-maximum (fwhm) values of 24-36 nm. Hydrazine (N2H4) was used to maintain oxygen-free conditions, allowing the reaction vessel to be open to air. The properties of the QDs were controlled using the thiol ligands, 3-mercaptopropionic acid (MPA), thiolglycolic acid (TGA), and L-glutathione (GSH). On the basis of optical spectra, linear three-carbon MPA attenuated nucleation and growth, yielding small ZnSe QDs with a high density of surface defects. In contrast, TGA and GSH produced larger ZnSe QDs with lower surface defect densities. The absorption spectra show that growth was more uniform and better controlled with linear two-carbon TGA than branched bifunctional GSH. After 20 min of growth TGA-capped ZnSe had an average diameter of 2.5 nm based on high-resolution transmission electron microscopy images; these nanocrystals had an absorbance peak maximum of approximately 340 nm (3.65 eV) and a band gap PL emission peak at 372 nm (3.34 eV). Highly fluorescent ZnxCd1-xSe QDs were fabricated by adding a Cd-thiol complex directly to ZnSe QD solutions; PL peaks were tuned in the blue range (400-490 nm) by changing the Zn to Cd ratio. The Cd-bearing nanocrystals contained proportionally more Se based on X-ray photoelectron spectroscopy, and Cd-Se bonds had ionic character, in contrast to primarily covalent Zn-Se bonds.

Preparation of Hydrophobic Quantum Dots Using Oleylamine-Hydrogen Selenide Complex As Precursor

Aqueous synthesis of CdSe and CdSe/CdS quantum dots with controllable introduction of Se and S sources

Preparation and Properties of High-quality CdSeS Alloyed Quantum Dots in Liquid Paraffin

Photo-assisted synthesis of highly fluorescent ZnSe(S) quantum dots in aqueous solution

Preparation of stable, water-soluble, highly luminescence quantum dots with small hydrodynamic sizes

Preparation of Quantum Dot Light-emitting Diodes Based on the Quantum Dots-CBP Hybrid

A Facile Route for Highly Efficient Color-Tunable Cu-Ga-Se/ZnSe Quantum Dots

Water-Based Route To Ligand-Selective Synthesis Of Znse And Cd-Doped Znse Quantum Dots With Tunable Ultraviolet A To Blue Photoluminescence

Synthesis of CdSe Quantum Dots (qds) in the Water

A simple hydrothermal route for synthesizing SnO<sub>2</sub> quantum dots

Significant Improvement in Photoluminescence of ZnSe(S) Alloyed Quantum Dots Prepared in High Ph Solution

Design and Fabrication of a Geometrically Ordered Hydrophobic Interlayer to Prepare High-Quality QD/SiO2 for Cell Imaging

A robust ligand exchange approach for preparing hydrophilic, biocompatible photoluminescent quantum dots

Highly Luminescent and Photostable Core/Shell/Shell ZnSeS/Cu:ZnS/ZnS Quantum Dots Prepared via a Mild Aqueous Route

A Facile Way to Fabricate CdSe Quantum Dots Coated with Silica and the Fluorescence Property

Synthesis and characterization of ZnSe and ZnSe/ZnS quantum dots for potential biomedical application

Preparation and Characterization of Overcoated Ii-Vi Quantum Dots

Synthesis of Highly Emissive CdSe Quantum Dots by Aqueous Precipitation Method

Preparation of ZnSe Quantum Dots Embedded in SiO2 Thin Films by Sol–gel Process

Aqueous synthesis of highly monodispersed thiol-capped CdTe quantum dots through electrochemical approach.

A Facile Synthesis of Small-Sized, Highly Photoluminescent, and Monodisperse CdSeS QD/SiO(2) for Live Cell Imaging.