Abstract:SnO 2 quantum dots, ranging from 10 to 30%, were combined with ZnO nanosheets to create a heterojunction photocatalyst. This composite was generated using a basic hydrothermal method, which was then followed by high-temperature calcination to enhance the photocatalytic activity of ZnO. The results showed that the synthesized SnO 2 nanoparticles with tetragonal rutile phase and ZnO nanosheets with hexagonal fibrillar zincite phase, the coupling of SnO 2 quantum dots and ZnO nanosheets improved the separation efficiency of the photogenerated carriers, and at the same time broadened the photoresponse range. Through the degradation of the organic dye Rhodamine B (RhB), the best photocatalytic activity was found at 20% amount of SnO 2 in the composite sample (SZ-2), and the degradation efficiency of RhB reached 96.5% at the light irradiation time of 100 min. In addition, an in-depth study of the photocatalytic mechanism of the constructed heterojunction by active group trapping experiments, and the results showed that •O 2 − and h + were the main active substances in this degradation system. Meanwhile, the SZ-2 photocatalyst was tested for five cycles, and the degradation efficiency of the 5th cycle was 72%. The cycle test indicates that the SZ-2 sample is highly stable and reusable. Therefore, the results showed that the prepared SnO 2 /ZnO heterojunction photocatalysts are suitable materials for degrading organic dyes.

A simple hydrothermal route for synthesizing SnO<sub>2</sub> quantum dots

A Simple and Novel Low-Temperature Hydrothermal Synthesis of ZnO Nanorods

Sub-2 Nm SnO2 Nanocrystals: A Reduction/oxidation Chemical Reaction Synthesis and Optical Properties

A Novel Hydrothermal Route to Synthesize Solid SnO 2 Nanospheres and Their Photoluminescence Property

Hydrothermal synthesis, characterization and properties of SnS nanoflowers

Facile hydrothermal synthesis of hydrotropic Cu2ZnSnS 4 nanocrystal quantum dots: Band-gap engineering and phonon confinement effect

A Facile Hydrothermal Route to the Synthesis of ZnIn2S4 Quantum Dots in the Presence of Thioglycolic Acid and Investigation Its Light Harvesting Application

Sequential Occurrence of ZnO Nanopaticles, Nanorods, and Nanotips During Hydrothermal Process in a Dilute Aqueous Solution

Amino acid-assisted hydrothermal synthesis and photocatalysis of SnO 2 nanocrystals

Synthesis of novel SnO2 quantum cubes and their selfassembly

Hydrothermal Synthesis of Zn2SnO4 Nanorods in the Diameter Regime of Sub‐5 Nm and Their Properties.

Hydrothermal synthesis of Z-type SnO2 quantum dot-modified ZnO nanosheets with enhanced photocatalytic activity

Facile Synthesis and Optical Property of SnO2 Flower-Like Architectures

Hydrothermal Synthesis of Lead Zirconate Titanate Nearly Free-Standing Nanoparticles in the Size Regime of about 4 Nm

Hydrothermal preparation and characterization of Zn2SnO4 particles

SnO2 Quantum Dots and Quantum Wires: Controllable Synthesis, Self-Assembled 2D Architectures, and Gas-Sensing Properties.

A novel method to prepare nanocrystalline SnO2

Zno Quantum Dots Synthesized by A Vapor Phase Transport Process

Ligand-assisted solvothermal precipitation synthesis of quantum-sized SnO2 nanoparticles and their application in quantum dot light emitting diodes

Synthesis of Monodispersed SnO2 Microspheres Via Solvothermal Method

Hydrothermal synthesis of SnO2 nanoflower arrays and their optical properties