Abstract:As a wide band-gap semiconductor，SnO2 films have attracted much attention due to their novel optical and electronic properties. It has been reported that the physical properties can be quite different when the size of SnO2 is reduced to nanometer scale due to the large surface-to-volume ratio and the quantum size effects，which may be applied in many kinds of devices, such as solar cells sensors. etc. It is interesting to study the synthesis of SnO2 nanoparticles and their physics properties. In the present work，a soft chemical technique was used to prepare SnO2 nanoparticles with uniform size and good crystallization in alkalescent solution. The surfactant was added during the preparation process to control the growth and agglomeration of crystal precipitates in the solution. X-ray diffraction spectra and transmission electron microscopy were used to characterize the structures of SnO2 nanoparticles before and after thermal annealing. It was found that the nanocrystalline SnO2 particles can be formed by the present technique and the size is about 4 nm with good crystallinity. With changing the preparation parameters，the size of nanocrystalline SnO2 particles is changed. Post thermal annealing at various temperatures （400—1000 ℃） can promote the crystallization and the size of formed particles was increased with increasing annealing temperature. Optical absorption spectra were used to see the change of the optical properties for samples prepared under different conditions. It was found that the optical band gap is enlarged in nanocrystalline SnO2 particles compared with its bulk counterpart, which can be attributed to the quantum confinement effect. The red-shift of the optical band gap with the particle size supported the quantum size effect. A broad photoluminescence band in the range of 350—750 nm can be detected in the annealed samples and the intensity was significantly enhanced after the thermal annealing. The luminescence peak energy was kept at 390 nm which was independent of the particle size. This luminescence band can be ascribed to the luminescence center associated with the oxygen vacancies on the SnO2 particle surface.

Hydrothermal synthesis of SnO2 nanoflower arrays and their optical properties

Facile synthesis of SnO2 nanograss array films by hydrothermal method

Facile Synthesis and Optical Property of SnO2 Flower-Like Architectures

Hydrothermal synthesis, characterization and properties of SnS nanoflowers

Template-free Hydrothermal Synthesis of Single-Crystalline SnO 2 Nanocauliflowers and Their Optical Properties

Hydrothermal synthesis and characterization of novel flower-like zinc-doped SnO2 nanocrystals

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Hydrothermal synthesis and characterization of SnO2 nanoparticles

A Novel Hydrothermal Route to Synthesize Solid SnO 2 Nanospheres and Their Photoluminescence Property

Synthesis and Optoelectrical Properties of SnO 2 Nanospheres Derived by Microwave-Assisted Hydrothermal Method

Study on structural and optical properties of Sn-doped ZnO nanoarrays

Hydrothermal Synthesis and Gas-Sensing Properties of Flower-Like Sn3o4

One-step Synthesis of Novel Hierarchical Flower-Like SnO2 Nanostructures with Enhanced Photocatalytic Activity

Sub-2 Nm SnO2 Nanocrystals: A Reduction/oxidation Chemical Reaction Synthesis and Optical Properties

Facile fabrication of transparent SnO2 nanorod array and their photoelectrochemical properties

Synthesis,structures and Luminescence Properties of SnO2 Nanoparticles

Hydrothermal Synthesis of Novel Hierarchical Flower-Like SnO2 with Enhanced Visible-Light-Driven Photocatalytic Activity

Evolution of SnO2 Nanoparticles into 3D Nanoflowers Through Crystal Growth in Aqueous Solution and Its Optical Properties

Synthesis and optical properties of SnO2 nanorods

Synthesis and Field-Emission of Aligned SnO 2 Nanotubes Arrays

Optical Properties of Tin Monoxide Nanoshells Prepared Via Self-Assembly