Dielectric Relaxations in Ba(Fe1∕2Ta1∕2)O3 Giant Dielectric Constant Ceramics

Z. Wang,X. M. Chen,L. Ni,Y. Y. Liu,X. Q. Liu

DOI: https://doi.org/10.1063/1.2711767

IF: 4

2007-01-01

Applied Physics Letters

Abstract:Dielectric relaxations of Ba(Fe1∕2Ta1∕2)O3 ceramics were investigated and discussed over a broad temperature and frequency range. Two dielectric relaxations following Arrhenius law were observed at 153–382 and 440–623K, where there was a giant dielectric constant step between them. The frequency dependent rapid drop of dielectric constant at 153–382K was nearly a Debye relaxation with the intrinsic nature, while the high temperature dielectric relaxation with an extremely high dielectric constant peak and very strong frequency dispersion was attributed to the defect ordering but not a typical relaxor ferroelectric behavior. The O2 annealing almost completely suppressed the dielectric peak and subsequently extended the giant dielectric step, while the low temperature dielectric relaxation and the magnitude of such step were not obviously affected.