Dielectric relaxation and polar phonon softening in relaxor ferroelectric PbMg_(1/3)Ta_(2/3)O_3

S.Kamba,D.Nuzhnyy,S.Veljko,V.Bovtun,J.Petzelt,Y.L.Wang,J.Levoska,M.Tyunina,J.Macutkevic,N.Setter,J.Banys

DOI: https://doi.org/10.1063/1.2784972

2007-07-13

Abstract:Relaxor ferroelectric PbMg_1/3Ta_2/3O_3 ceramics and thin films were investigated by means of broad-band dielectric, time-domain terahertz (THz) and Fourier-transform infrared (IR) spectroscopy in the frequency range 100 Hz - 90 THz at temperatures 100 - 490 K, the THz and IR spectra were studied from 20 to 900K. Diffused and strongly temperature dependent peak in the complex permittivity is caused by a dielectric relaxation due to the dynamics of polar clusters. The relaxation appears below Burns temperature T_d in the THz range, slows down on cooling through the microwave and MHz range and anomalously broadens. The shortest and longest relaxation times of the distribution of relaxation times follow Arrhenius and Vogel-Fulcher law, respectively. The degree of B-site order has only a small influence on the parameters of the dielectric relaxation and almost no influence on the phonon parameters. Below T_m ~ 180K, the distribution of relaxation frequencies becomes broader than our experimental spectral range and frequency independent dielectric losses develop below 100 GHz in the spectra. Although the macroscopic crystal structure is cubic, IR spectra give evidence about the lower local symmetry which can be assigned to the presence of polar clusters below T_d. Infrared spectra above T_d still reveal more modes than predicted by selection rules in the paraelectric phase of the Fm-3m space group so that we suggest selection rules which take into account chemical inhomogeneity in the beta''-perovskite sublattice.

Materials Science

What problem does this paper attempt to address?

### What problems does this paper attempt to solve?

This paper mainly studied the dielectric relaxation and polar phonon softening phenomena in the relaxor ferroelectric PbMg\(_{1/3}\)Ta\(_{2/3}\)O\(_3\) (PMT). Specifically, the author explored the following problems through a wide range of experimental methods (such as broadband dielectric measurement, terahertz - time - domain spectroscopy, and Fourier - transform infrared spectroscopy):

1. **Origin and characteristics of dielectric relaxation**:
- The researchers found that below the Burns temperature \( T_d \), a diffuse and strongly temperature - dependent dielectric relaxation peak caused by the dynamics of polar clusters appeared in PMT.
- This relaxation gradually slows down during the cooling process and exhibits different characteristics in different frequency ranges.

2. **Relaxation time distribution and its temperature - dependence**:
- Research shows that the shortest and longest relaxation times follow the Arrhenius and Vogel - Fulcher laws respectively.
- The distribution function \( f(\tau) \) of relaxation time becomes very wide at low temperatures, causing the dielectric loss to hardly change with frequency in the low - frequency region.

3. **Softening behavior of polar phonons**:
- It was observed in the infrared spectrum that the polar phonon mode partially softened when heated to \( T_d \) and hardened again when above \( T_d \), which is related to the existence of local ferroelectric instability.

4. **Effect of chemical order on dielectric response**:
- It was found that the chemical order at the B - site has a minor effect on dielectric relaxation parameters and almost no effect on phonon parameters.
- Although a certain degree of 1:1 chemical order can be achieved through appropriate heat treatment, this has no significant effect on dielectric relaxation.

5. **Dielectric response in the high - frequency region**:
- The research was also extended to the high - frequency regions (> 100 GHz) of THz and infrared spectra to fully understand the relaxation behavior at high temperatures.

6. **Selection rules and local symmetry**:
- The researchers proposed a new selection rule, taking into account the chemical inhomogeneity in the β'' - perovskite sublattice, to explain more optical vibration modes observed at high temperatures.

Through these studies, the author aims to deeply understand the dielectric relaxation mechanism in the relaxor ferroelectric PMT and its relationship with polar nano - regions, providing theoretical basis and technical support for the development of high - performance ferroelectric materials.