Dielectric Relaxor Evolution and Frequency‐Insensitive Giant Strains in (bi0.5na0.5)tio3‐modified Bi(Mg0.5Ti0.5)O3–PbTiO3 Ferroelectric Ceramics

Wanli Zhao,Ruzhong Zuo,Donggeng Zheng,Longtu Li

DOI: https://doi.org/10.1111/jace.12841

IF: 4.186

2014-01-01

Journal of the American Ceramic Society

Abstract:The 0.45Bi(Mg0.5Ti0.5)O3–(0.55 − x)PbTiO3–x(Bi0.5Na0.5)TiO3 (BMT–PT–xBNT) ternary solid solution ceramics were prepared via a conventional solid‐state reaction method; the evolution of dielectric relaxor behavior and the electrostrain features were investigated. The XRD and dielectric measurements showed that all studied compositions own a single pseudocubic perovskite structure and undergo a diffuse‐to‐relaxor phase transition owing to the evolution of the domain from a frozen state to a dynamic state. The formation of the above dielectric relaxor behavior was further confirmed by a couple of measurements such as polarization loops, polarization current density curves, as well as bipolar strain loops. A large strain value of ~0.41% at a driving field of 7 kV/mm (normalized strain d33* of ~590 pm/V) was obtained at room temperature for the composition with x = 0.32, which is located near the boundary between ergodic and nonergodic relaxor. Moreover, this electric field‐induced large strain was found to own a frequency‐insensitive characteristic.