Study Of Mechanical And Dielectric Spectrum In Yfe1-Xmnxo3 Ceramics
Weili Zhu,Ju He,Yaming Jin,Ruixia Ti,Tingting Xu,Chen Yue,Fengzhen Huang,Xiaomei Lu,Feng Yan,Jinsong Zhu
DOI: https://doi.org/10.1063/1.4862301
IF: 2.877
2014-01-01
Journal of Applied Physics
Abstract:The mechanical spectra of Mn-substituted yttrium orthoferrite YFe1-xMnxO3 (x = 0, 0.2, 0.3, 0.4) ceramics were performed at kilohertz from 100 to 360 K. Two internal friction (IF) peaks are observed around 150K and 230 K, respectively, and both the IF peaks exhibit frequency dispersion behavior. The IF peak around 150K is associated with a step increase in the modulus and its mechanical relaxation rate follows the Vogel-Fulcher relation with tau(0) - 4.45 x 10(-11) s, E-alpha - 0.03 eV, and T-VF - 155 K. This IF peak can be explained in terms of a freezing of oxygen vacancies after excluding the possible magnetic spin glass transition. Another IF peak around 230K presents a relaxation behavior and it follows Arrhenius law. Furthermore, the relaxation behavior was verified by the dielectric spectrum and it can be ascribed to the charge carrier hopping between Fe2+ and Fe3+. (C) 2014 AIP Publishing LLC.