Equiaxed Nd–Fe–B Fine Powder with High Performance Prepared by Mechanical Alloying

Jingzhi Han,Shunquan Liu,Xiaodong Zhang,Honglin Du,Ming Yue,Xubo Liu
DOI: https://doi.org/10.1063/1.2709408
IF: 2.877
2007-01-01
Journal of Applied Physics
Abstract:Equiaxed Nd11.9Fe76.9Co4.8B5.9Zr0.5 fine powders with high performance are fabricated by mechanical alloying method in this work. The mechanically alloyed Nd–Fe–B powders have a Br of 8.7kGs, an Hci of 10283Oe, and a (BH)max of 15.03MGOe. Moreover, it is notable that the Mr∕Ms ratio of these powders reaches 0.73. According to x-ray diffraction and high-resolution transmission electron microscopy studies, the powders consist of two phases, the Nd2Fe14B and α-Fe phase, and an average grain size of both phases is about 30nm. These results show that the remanence enhancement of the powders may be from the exchange coupling among Nd2Fe14B grains as well as between Nd2Fe14B and Fe grains. Scanning electron microscopy studies show that the mechanically alloyed powders are equiaxed, and the powders’ size distribution is very broad. Further investigation using a laser scattering particle size distribution analyzer shows that the size distribution of the powders is bimodal, and the mean size is merely about 16μm. Finally, thermal stability of the above powders is measured, and the initial irreversible flux loss of the above powders is about 5% at 120°C at a permeance of 2. Based on the above results, it is inferred that the equiaxed Nd–Fe–B fine powders made by the mechanical alloying process are suitable for preparing injection-molded magnets.
What problem does this paper attempt to address?