Effects of in situ Mg-Sialon and β-Sialon on the microstructure and properties of MgAl2O4-SiC composites
Yaochen Si,Hongxia Li,Shixian Zhao,Honggang Sun,Yihao Du,Chenwei Gu,Mengqiang Wang,Ruida Wang,Suhang Zhou,Yong Li
DOI: https://doi.org/10.1016/j.jeurceramsoc.2023.11.018
IF: 5.7
2023-11-01
Journal of the European Ceramic Society
Abstract:MgAl2O4-SiC composites were prepared under flowing nitrogen at 1500 °C by using MgAl2O4 powder, SiC powder, Al powder and Si powder as raw materials. Through microstructural observation and analysis, the effects of in situ Mg-Sialon and β-Sialon with different amounts of Si powder addition were investigated in this paper. The results show that the samples without Si addition main contained MgAl2O4, SiC and well development plate structure Mg-Sialon phase. After addition of Si powder, not only the above three phases appeared, but also β-Sialon phase appeared. Meanwhile, with increasing Si contents, the content of β-Sialon phase increased and samples were more dense, limiting the development of the plate structure Mg-Sialon phase. With increasing Si content from 0 wt% to 20 wt%, the apparent porosity shows decreased trend, while the bulk density and cold module of rupture show increased. The samples with 20 wt% Si addition can get the minimum apparent porosity (33.5 %), maximum bulk density (2.13 g•cm−3) and cold module of rupture (87.0 MPa). Besides, the formation mechanism of Mg-Sialon and β-Sialon was discussed in detail and the role of Si was elucidated.
materials science, ceramics