Abstract:A series of Fe-Co-Ni alloy/Co0.5Ni0.5Fe2O4 composite nanofibers with average diameters from 67 to 85 nm and various alloy contents were synthesized by hydrogen-thermal reduction of Co0.5Ni0.5Fe2O4 nanofibers prepared via sol-gel methode and electrospinning. The obtained nanofiber samples were characterized by TG-DTA, XRD, FE-SEM, TEM and VSM. The results show that the mass fraction of Fe-Co-Ni alloys in the reduced products progressively increases from 15.2%to about 95.7%with increasing the reduction temperature of Co0.5Ni0.5Fe2O4 nanofibers from 290℃to 350 ℃. Meanwhile, the fiber diameter gradually decreases and the fiber surface morphology evolves toward the bead-like structures. The magnetic field dependence of the magnetization behaves as if the as-prepared Fe-Co-Ni alloy/Co0.5Ni0.5Fe2O4 composite nanofibers are single-phase magnetic materials, which indicates that the two magnetic phases in composites are effectively exchange-coupled and that the magnetization of both phases reverses cooperatively. The saturation magnetization and remanence of the samples increase monotonically with the increase of Fe-Co-Ni alloy content, while the corresponding coercivity shows a trend of first increase and then decrease. The formation of Fe-Co-Ni alloy phase can not only obviously improve the soft magnetic performance of the composite nanofibers, but also effectively realize the wide-range control for the magnetic parameters through adjusting the Fe-Co-Ni alloy content in composites.

Microemulsion Synthesis and Characterization of Fe-Co-Ni Alloy Nanoparticles

Synthesis of iron–nickel nanoparticles via a nonaqueous organometallic route

Positive Microemulsion Synthesis and Magnetic Property of Amorphous Multicomponent Co-, Ni- and Cu-based Alloy Nanoparticles

Preparation of nanosized particles of FeNi and FeCo alloy in solution

Preparation and Characterization of Iron-Nickel Alloy Nanoparticles

Preparation of Nanostrured Fe - Co Alloy

Synthesis and Characterization of Nanoscale Fe/Ni Alloy Particles by Hydrothermal Method

Preparation of Cu-Ni alloy nanocrystallites in water-in-oil microemulsions.

Preparation and Characterization of Monodisperse Fe Nano-particles

Hydrothermal Synthesis of Ni-Co-Cu Alloy Nanoparticles from Low Nickel Matte

Synthesis and Characterization of Nanostructured Fe-Ni Alloy Whisker

Controlled syntheses of FeNi3 alloy nanostructures via reverse microemulsion-directed hydrothermal motheds

Sonochemical synthesis, structural and magnetic properties of air-stable Fe/Co alloy nanoparticles

The synthesis of iron–nickel alloy nanoparticles using a reverse micelle technique

Preparation of CoFe2O4 Nanoparticles by Microemulsion Approach

Preparation and Properties of Fe-Co-Ni Alloy/co0.5ni0.5fe2o4 Magnetic Composite Nanofibers

Synthesis and Characterization of CoFe 2 O 4 Nanoparticles

Preparation and Characterization of Nano-Fe50ni50 Alloy Powder by Chemical Co-Precipitation Hydrogen Reducing Process

Synthesis of Feco Nanoparticles from Feo(Oh) and Co3o4 Using Oleic Acid As Reduction Agent

Preparation and application of nano-Ni–Co alloy

Preparation and Characterization of Feco Alloy Nanoparticles