Abstract:The main purpose of this work is to explore the influences of microstructures on the magnetic properties, as well as the formation mechanism of -Fe2O3/NiO core/shell nanoflowers. The synthesis of nanoflower-like samples includes three processes. Firstly, Fe3O4 nanospheres are synthesized by the solvothermal reaction of FeCl3 dissolved in ethylene glycol and NaAc. Secondly, Fe3O4/Ni(OH)2 core/shell precursor is fabricated by solvothermal method through using the early Fe3O4 spheres and Ni(NO3)26H2O in an ethanol solution. Finally, the precursor Fe3O4/Ni(OH)2 is calcined in air at 300 ℃ for 3-6 h, and therefore resulting in -Fe2O3/NiO core/shell nanoflowers. Their microstructures are characterized by using XRD, XPS, SEM, HRTEM and SAED techniques. The results show that the final powder samples are -Fe2O3/NiO with typical core/shell structure. In this core/shell system, the -Fe2O3 sphere acts as core and the NiO acts as shell, which are comprised of many irregular flake-like nanosheets with monocrystalline structure, and these nanosheets are packed together on the surfaces of -Fe2O3 spheres. The calcination time of Fe3O4/Ni(OH)2 precursor has significant influences on the grain growth, the NiO content and the compactness of NiO shells in the -Fe2O3/NiO core/shell system. VSM and SQUID are used to characterize the magnetic properties of -Fe2O3/NiO core/shell nanoflowers. The results indicate that the 3 h-calcined sample displays better ferromagnetic properties (such as higher ms and smaller HC) because of their high -Fe2O3 content. In addition, as the coupling interaction between the FM -Fe2O3 and AFM NiO components, we observe that the -Fe2O3/NiO samples formed in 3 h and 6 h display certain exchange bias (HE=20 and 46 Oe, respectively). Such a coupling effect allows a variety of reversal paths for the spins upon cycling the applied field, and thereby resulting in the enhancement of coercivity (HC(FC)=252 and 288 Oe, respectively). Further, the values of HE and HC for the former are smaller than those of the latter, this is because of the AFM NiO content in 6 h-calcined sample much higher than that in 3 h-calcined sample. Especially, the temperature dependences of the magnetization M of the two samples under both ZFC and FC conditions indicate that an extra anisotropy is induced. In a word, the size effect, NiO phase content, and FM-AFM (where FM denotes the ferromagnetic -Fe2O3 component, while AFM is the antiferromagnetic NiO component) interface coupling effect have significant influence on the magnetic properties of -Fe2O3/NiO core/shell nanoflowers.

The synthesis of iron–nickel alloy nanoparticles using a reverse micelle technique

Synthesis of iron–nickel nanoparticles via a nonaqueous organometallic route

Size- and Structure-Controlled Synthesis and Characterization of Nickel Nanoparticles

Chemical Synthesis of Monodisperse Fe-Ni Nanoparticles Via A Diffusion-Based Approach

Iron-Nickel Alloy with Starfish-like Shape and Its Unique Magnetic Properties: Effect of Reaction Volume and Metal Concentration on the Synthesized Alloy

Preparation of hexagonal close-packed nickel nanoparticles via a thermal decomposition approach using nickel acetate tetrahydrate as a precursor

Employing the Microemulsion Synthesis Technique to Investigate the Structural and Magnetic Properties of Multicomponent Ferrite Nanoparticles

Controlled Synthesis of Magnetic Spinel-Type Nickel Ferrite Nanoparticles by the Interface Reaction and Hydrothermal Crystallization

$\mathrm{Fe}_{1-x}\mathrm{Ni}_x$ Alloy Nanoparticles Encapsulated inside Carbon Nanotubes: Controlled Synthesis, Structure and Magnetic Properties

Microscale Interface Synthesis of Ni-B Amorphous Nanoparticles from NiSO4 by Sodium Borohydride Reduction in Microreactor

Colloidal synthesis of nanoparticles: from bimetallic to high entropy alloys

Size-controlled Synthesis of Nickel Nanoparticles

A Novel Sol–gel Process to Facilely Synthesize Ni3Fe Nanoalloy Nanoparticles Supported with Carbon and Silica

A Low Temperature Mechanochemical Synthesis And Characterization Of Amorphous Ni-B Ultrafine Nanoparticles

Synthesis and characterization of Fe3O4/SiO2 core-shell nanoparticles in reverse micelles

Synthesis and characterization of core-shell structure silica-coated Fe29.5Ni70.5 nanoparticles

Carbon Monoxide-Assisted Size Confinement Of Bimetallic Alloy Nanoparticles

Rapid Synthesis Of Nickel Ferrite Nanoparticles By The Molten Salt Method

Synthesis, Microstructure, and Magnetic Properties of -Fe2o3/nio Core/shell Nanoflowers

The Structure of Modified Fe-Ni Bioxide Composite Nanoparticles Using Fe(NO 3 ) 3

A Facile Route for the Preparation of Monodisperse Iron nitride at Silica Core/shell Nanostructures