Preparation of Fe3O4 Nanoparticles Coated with Surfactant and Its Application in Oilfield Produced Water Treating
Cui-Yu JIANG,Wei ZHU,Hao SONG,Hui-Ying LIU,Yi GENG,Lu-Ning WU,Xiao-Bo ZHANG
DOI: https://doi.org/10.19346/j.cnki.1000-4092.2010.03.022
2010-01-01
Abstract:The magnetic nanoparticles were synthesized by the chemical coprecipitation of ferrouschloride and ferricchloride.The obtained magnetic nanoparticles were coated with cationic surfactant(901).The optimum reaction conditions was established as follows: pH=7,901 dosage of 15 g/L,reaction temperature 60℃,reaction time 30 min,Fe3O4/901 in concentration ratio 4∶1.The saturation magnetization of Fe3O4 particles was 59.61 emu/g,with a supper paramagnetic property.TEM images showed that the average size of Fe3O4 particles was 20 nm,and that of Fe3O4/901 was about 25 nm.The structure of Fe3O4 nanoparticles coated with 901 was characterized by IR.A complex of Fe3O4 /901,polyaluminum chloride(PAC) and cationic polymer was used to treat oily sewage from Gusilian in Shengli oilfield.The results showed that the oil content decreased from 1078.3 mg/L to 14.5 mg/L,and the suspended solids content decreased from 146 mg/L to 20 mg/L,while the reaction time needed was as short as one minute.Compared with the results obtained by PAC and cationic polymer,the effect of oil removal had been promoted for 3%,and the content of suspended solids had been decreased for 79%,with a higher speed of deoiling.