Corrosion Fatigue of Die-Cast Magnesium Alloys

LIU Ma-bao,LEI Jun,GAO Yu-xia,ZHANG Ying-jie,QI Yan-jie,SUO Jian-qin

DOI: https://doi.org/10.3969/j.issn.1005-5053.2007.01.017

2007-01-01

Abstract:The fatigue properties of die-cast magnesium alloys AM50HP and AZ91HP were determined in ambient air and in 3.5% sodium chloride solution,respectively.It is found that fatigue cracks initiate from the casting pores within the specimen and near the surface in both environments depending on the relative pore size,and the S-N curves of both alloys are steeper in corrosive environment than in ambient air.Both die-cast magnesium alloys do not have endurance limits in 3.5% NaCl solution,whereas endurance limits could be detected in ambient air,which are about 90MPa and 100MPa for AZ91HP and AM50HP respectively.The die-cast magnesium alloy AM50HP shows a higher sensitivity to the action of 3.5% NaCl solution in comparison with AZ91HP,and the corrosion fatigue behaviour of both die-cast magnesium alloys correlates with their mechanochemical behaviour.The latter was studied by the polarization measurements of the dissolution rate of strained magnesium alloys.