Fabrication of NiO and TiO 2 supported nano calcium carbonate and its effect on the flame retardancy and thermal stability of epoxy resin composites
Zheng Li,Zuodong Qin,Chunxuan Li,Guimei Zhang,Aozheng Zhang,Sisi Li,Guoqi Liang,Xin Wang,Wufei Tang
DOI: https://doi.org/10.1016/j.polymdegradstab.2023.110296
IF: 5.204
2023-02-16
Polymer Degradation and Stability
Abstract:Nano calcium carbonate (CaCO 3 ) was successfully treated by tetrabutyl titanate sol together with nickel hydroxide, followed by calcination to form a new kind of flame retardant (Ni-TiO 2 @CaCO 3 ). After study of the Ni-TiO 2 @CaCO 3 structure, it was then introduced into epoxy resin (EP) to improve the flame retardancy and thermal stability. The results shown that NiO and TiO 2 were supported on the surface of the CaCO 3 , and 5 wt% CaCO 3 could enhance the flame retardancy and Ni-TiO 2 @CaCO 3 further increased the flame retardancy of the EP composites. In the cone calorimeter test (CCT), the values of the peak heat release rate (pHRR) and smoke production rate (pSPR) were reduced to 769 kW/m 2 and 0.32 m 2 /s by CaCO 3 from 1101 kW/m 2 and 0.39 m 2 /s of the raw EP respectively. Moreover, pHRR and pSPR values were further decreased to 511 kW/m 2 and 0.25 m 2 /s by Ni-TiO 2 @CaCO 3 respectively. Although the degradation temperature values were lower than that of the control EP, the temperature values at 5 and 50% mass loss for Ni-TiO 2 @CaCO 3 /EP composites were improved compared to the EP. In addition, the char residues value of the Ni-TiO 2 @CaCO 3 / EP composite (23.5%) was obviously improved compared to that of the EP (13.0%) and CaCO 3 / EP composite (16.4%). In addition, the flame retardancy mechanism of the Ni-TiO 2 @CaCO 3 / EP composite was thoroughly analyzed by TGA-FTIR, FITR and Raman methods. This work provides a promising evaluation strategy for utilizing CaCO 3 and its derivatives for possible treatment of EP to enhance its flame retardancy and thermal stability.
polymer science