Study on Bond Strength of Epoxy Resin Structural Adhesive Modified by Nanosize Materials

PENG Bo,CHEN Jian-cong,CHEN Jian-ming
2007-01-01
Abstract:The bond strength of structural adhesive modified by nanosize SiO2,nanosize CaCO3 and oganic-montmorillonte(OMMT) was advanced considerably.Result showed that,when nanosize SiO2,nanosize CaCO3 and OMMT content were 5%,20%,10%,the steel-steel shear strength increased 23.2%,39.3% and 63.0%,compared with the pure epoxy base,respectively.Steel-steel shear strength of the adhesive was successfully raised to 30 MPa curing at 25 ℃ by combining nanosize SiO2 and nanosize CaCO3.XRD result showed that interlayer space of OMMT changed from 2.1 nm to 8.8 nm at least by intercalation compounding.SEM result showed that,because these nanophase materials could induce many microcrack in the base,the bond strength of structural adhesive was advanced.