Abstract:A critical determination of a phase diagram of the Zn-Fe binary system was carried out by EPMA analysis for skillfully prepared and equilibrated two-phase alloys for solid phases and by EDS areal analysis for the Fe solubility in the heterogeneously solidified liquid phase instead of the conventional diffusion couple method. It was newly confirmed that equilibrium compositions of intermetallic compounds tend to shift toward the Fe side compared to the previous phase diagram on the whole and that the solubility ranges of the Γ-Fe3Zn10 and Γ1-Fe11Zn40 phases are much narrower than those in the literature. The critical composition of the second-order order-disorder transition between δ1k-FeZn7 and δ1p-FeZn10 at high temperature was estimated by Vickers hardness measurement. Furthermore, the phase separation, i.e., the first-order transition, between the δ1k and δ1p phases in the low temperature region was directly found out and its equilibrium compositions were confirmed by EPMA analysis for the two-phase microstructures. The width of the δ1k + δ1p two-phase region at 500 °C is only 0.5 at.% and the δ1p decomposes into the δ1k and ζ-FeZn13 phases via a eutectoid reaction at a temperature between 455 °C and 445 °C. While being mostly coincident with those in the previous literature at temperatures between 1000 °C and 600 °C, the solubility of Fe in the liquid (L) Zn phase is about twenty times larger than the assessed value in the literature at temperatures below 500 °C. A eutectic reaction, L → ζ + (ηZn), was confirmed to occur by precise EPMA analysis and DSC measurement.

Phase equilibria in the Zn-Fe-S system at 450 °C

Experimental study of the phase relations in the Fe–Cr–Si ternary system at 700°C

Experimental determination of phase diagram in the Zn-Fe binary system

Phase Equilibria in the Ni-Sn-Zn System at 500°C

Phase equilibria in the Fe-Ti-Zr system at 1023 K

Phase equilibrium diagram of the Hf-Fe-Sn system at 1070 K

Thermodynamic Evaluation of the Fe-Zn Binary System with Reference to the Latest Experimental Phase Diagram

Half‐Heusler Phase Related Structural Perturbations Near Stoichiometric Composition FeZnSb.

Phase equilibria in the Fe–Nb–Zr ternary system at 1,200 °C

Isothermal Section of Ternary Sn-Zn-Ni Phase Equilibria at 250 °C

Phase Equilibria In The Fe-Nb-Zr Ternary System At 1,200 A Degrees C

Thermodynamics of Solid and Liquid MnS–CrS–FeS Phase in Equilibrium with Molten Fe–Cr–Mn–S Alloy

Phase Equilibria of the Sn–Zn–Cu Ternary System

Phase equilibrium of Cd 1– x Zn x S alloys studied by first-principles calculations and Monte Carlo simulations

Phase equilibria of the Co-Ni-Zr system at 1198 K

Half-Heusler phase related structural perturbations near stoichiometric composition FeZnSb

Effect of Ni on Fe–FeS Phase Relations at High Pressure and High Temperature

Ag-Cu-Te Phase Equilibria Isothermal Sections at 600 °C and 400 °C

The High-Temperature Cu-Fe-S System: Thermodynamic Analysis and Prediction of the Liquid–Solid Phase Range

Isothermal Section Of Mn-Zr-Si Ternary System At 600 Degrees C

Phase Equilibria of the Fe–Nb–Ti System at 900 °C