Abstract:An effective design strategy for preparing highly transparent polyimide film with low dielectric constant is presented. The key to the strategy is to simultaneously introduce meta-substituted structure and trifluoromethyl in polymer chains. By using this design strategy, a highly transparent polyimide film with low-k was synthesized from 3,5-diaminobenzotrifluoride (m-TFPDA) and 4,4′-(hexafluoroisopropylidene) diphthalic anhydride (6FDA) through a two-step method. The obtained m-TFPDA/6FDA (CPI) film (∼30 µm) possesses high optical transparency (λcutoff=334 nm, T450nm=85.26%, Haze=0.31) and is close to colorless (L*=96.03, a*=−0.34, b*=2.12, yellow index=3.96). The intrinsic k and dielectric loss value of the film are 2.27 and 0.0013 at 10 kHz, respectively. More importantly, such low dielectric performance could remain stable up to 280 °C, and the film shows a low moisture rate (∼0.51%), which helps to maintain the low-k property stability in different humid environments. Meanwhile, the film also shows good thermal stability and mechanical properties, with a glass transition temperature (Tg) of 296 °C and the 5 wt% decomposition temperature (Td,5%) of 522 °C under N2. The tensile strength and tensile modulus of the film are 85.1 MPa and 1.96 GPa, respectively. In addition, the film is soluble in common solvents, which allows simple solution processing and low-cost, continuous roll-to-roll processes. This design strategy is beneficial to improving the transparency, lightening yellow color, lowering the dielectric constant and meanwhile maintaining the comprehensive properties of polyimide films, which is mainly due to the introduced meta-substituted and trifluoromethyl structures effectively inhibiting the transfer of charge transfer complex (CTC) effects and increasing the free volume of film. This design strategy could also be extended to other high-performance polymer systems.

Ultra-low-? Polyimide Hybrid Films Via Copolymerization of Polyimide and Polyoxometalates

Polyimide Foams with Ultralow Dielectric Constants

Preparation and Dielectric Properties of Polyimide/silica Nanocomposite Films Prepared from Sol–gel and Blending Process

Silica/polyimide Hybrids and Their Dielectric Properties. I. Preparation with an Improved Sol–gel Process with Poly(amic Acid) As the Precursor

PREPARATION AND STUDY ON STRUCTURE OF THE POLYIMIDE/SILICA HYBRID AND NANOCOMPOSITE FILMS

Mechanically Strong, Transparent Polyimide Composite Thin Films with a Low Dielectric Constant

Low dielectric constant ultrathin polyimide films alternated by poly(amic acid) salt/poly(allylamine hydrochloride)/imogolite through layer by layer deposition

Fluorinated polyimide/POSS hybrid polymers with high solubility and low dielectric constant

Highly Transparent and Colorless Polyimide Film with Low Dielectric Constant by Introducing Meta-substituted Structure and Trifluoromethyl Groups

Origin of Ultralow Permittivity in Polyimide/mesoporous Silicate Nanohybrid Films with High Resistivity and High Breakdown Strength

Ultra-low-permittivity, high hydrophobic, and excellent thermally stable fluoroelastomer/polyimide composite films employing dielectric reduction

Polyimide/mica hybrid films with low coefficient of thermal expansion and low dielectric constant

Polyimide Films Based on β-Cyclodextrin Polyrotaxane with Low Dielectric and Excellent Comprehensive Performance

Low Dielectric Constant Polyimide Hybrid Films Prepared by in Situ Blow-Balloon Method

Polyhedral oligosilsesquioxane-modified boron nitride enhances the mechanical properties of polyimide nanocomposites

Flexible Low Dielectric Polyimide/Fluorinated Ethylene Propylene Composite Films for Flexible Integrated Circuits

Polyimide/fluorinated silica composite films with low dielectric constant and low water absorption

Polyimide–polydimethylsiloxane Copolymers for Low‐dielectric‐constant and Moisture‐resistance Applications

Porous polyimide composite films containing mesoporous hollow silica nanospheres with ultralow dielectric constant and dissipation loss

Mesoporous polyetherimide thin films via hydrolysis of polylactide-b-polyetherimide-b-polylactide

Reduced coefficient of linear thermal expansion of colorless and transparent polyimide by introducing rigid-rod amide unit: synthesis and properties