Phase transformation in spodumene–diopside glass

H. Anmin,L. Ming,M. Dali

DOI: https://doi.org/10.1007/s10973-005-6941-z

IF: 4.755

2006-01-01

Journal of Thermal Analysis and Calorimetry

Abstract:In situ developments of platelike spodumene–diopside grains were obtained by controlled devitrification of the complex system Li 2 O–CaO–MgO–Al 2 O 3 –SiO 2 glass. The crystallization mechanisms of spodumene–diopside glass were measured by isothermal and non-isothermal processes using classical and differential thermal analysis techniques. The Avrami constant n was 2.0–2.1, indicating two-dimensional crystal growth and platelike grains. The crystalline phases precipitated first were high-quartz s.s. , then transformed to β-spodumene and diopside. The Flexural strength, fracture toughness and thermal shock resistance (in 20°C water) increased from 145 MPa, 1.3 MPa m 1/2 , 800°C (pure spodumene) to 197 MPa, 2.9 MPa m 1/2 and 920°C (spodumene–diopside) with low thermal expansion coefficient (from 3∼9·10 –7 to 11.8·10 –7 K –1 ). This mean in situ developments of platelike spodumene–diopside grains reinforced the low thermal expansion coefficient glass-ceramics.